Hanxia HX FPC 0.5-22P HYH2.0 flexible flat cable connector with UL 94V-0 LCP material certification

Name: Hanxia HX FPC 0.5-22P HYH2.0 flexible flat cable connector with UL 94V-0 LCP material certification
Brand: Hefei Purple Horn E-Commerce Co., Ltd.

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Product Description

Product Overview

This specification covers the 0.5mm Pitch FPC/FFC Connectors manufactured by Shenzhen Hanxia Electronic Co., Ltd. These connectors are designed for flexible flat cable applications.

Product Attributes

Brand: Hanxia Electronic (HX)
Origin: Shenzhen, China
Certifications: UL 94V-0 (for LCP material)

Technical Specifications

Item	Requirement	Test Condition
3. RATINGS
Rated Voltage (MAX)	AC/DC (Virtual value) 50Hz 50V
Rated Current (MAX)	0.5A
Ambient temperature Range	-25+85
4. PERFORMANCE
4.1 Electrical Performance
Contact Resistance	30 m MAX	Mate applicable FPC/FFC and measure by dry circuit, 20mV MAX, 10mA.
Insulation Resistance	500 M MIN	Mate applicable FPC/FFC and apply 500V DC between adjacent terminal or ground.
Dielectric Strength	No Breakdown	Mate applicable FPC/FFC and apply 200V AC (virtual value) for 1 minute between adjacent terminal or ground.
4.2 Mechanical Performance
Locking and Withdrawal Force	Locking: 1.96n (N) MAX Withdrawal: 0.49n (N) MIN	Insert and extract applicable FFC (0.3mm thickness) at the speed rate of 253mm/minute.
Terminal /Housing Retention Force	3.92N MIN	Pull the terminal at the speed rate of 25 3mm per minute.
4.3 Environmental Performance and Others
Repeated Insertion and Withdrawal	Contact Resistance: 60 m MAX	Insertion and withdrawal actuator up to 20 cycles at the speed rate of less than 10 cycles/minute (no power).
Temperature Rise	30 MAX	Carrying rated current load. (UL 498)
Vibration	Contact Resistance: 60 m MAX Discontinuity: 1 ms MAX	DC 1mA under power. Vibration along XYZ axes, Amplitude: 1.5mm P-P, Sweep time: 10-55-10Hz/min, Duration: 2 hours in each axis.
Shock	Appearance: No Damage Discontinuity: 1 ms MAX	DC 1mA under power. 490m/s {50G}, 3 strokes in each of the 6 directions.
Heat Resistance	Appearance: No Damage Contact Resistance: 60 m MAX	Mate applicable FPC/FFC, placed in 852 air for 96 hours, then returned to room temperature for 1-2 hours.
Cold Resistance	Appearance: No Damage Contact Resistance: 60 m MAX	Mate applicable FPC/FFC, placed in -402 air for 96 hours, then returned to room temperature for 1-2 hours.
Humidity	Appearance: No Damage Contact Resistance: 60 m MAX Dielectric Strength: Must meet 4.1.3 Insulation Resistance: 20 M MIN	Mate applicable FPC/FFC, placed in 402, 90-95% RH for 96 hours, then measured within 0.5 hours at room temperature.
Temperature Cycling	Appearance: No Damage Contact Resistance: 60 m MAX	5 cycles of: -553 for 30 minutes, then 852 for 30 minutes, with 10-15 minutes at normal temperature and humidity between cycles.
Salt Spray	Appearance: No Damage, Corrosion Contact Resistance: 60 m MAX	48 4 hours exposure to a salt spray from a 51% solution at 352. Post-test rinse with room temperature water and air dry.
SO2 Gas	Contact Resistance: 60 m MAX	24 hours exposure to 505ppm SO2 gas at 402.
NH3 Gas	Appearance: No Damage Contact Resistance: 60 m MAX	40 minutes exposure to NH3 gas evaporating from a 28% Ammonia solution.
Solderability	Solder Wetting: 95% coverage	Soldering Time: 20.5 sec. Soldering Temperature: 2455 at 0.2 mm from terminal tip.
Resistance to Soldering Heat	Appearance: No Damage, Deformation	Soldering Time: 305 sec. Soldering Temperature: 2455. Performed at least 5 times in a hot air furnace.
5. PRODUCT SHAPE, DIMENSIONS AND MATERIALS (Refer to drawing)
NAME	MATERIALS	REMARK
Main body	LCP UL 94V-0
Housing Lock	LCP UL 94V-0
Terminal Sit up	Phosphor Bronze	Surface plated with tin
Contact	Phosphor Bronze	Surface plated with tin