Robust connector hanxia HX USB3.1TYPE-C-16P FS designed for USB 3.1 Type C rated 20V 5A applications

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Product Description

Product Overview

This document outlines the specifications for the HX USB3.1TYPE-C-16P FS connector from Shenzhen Hanxia Electronic Co., Ltd. It details the product's mechanical, electrical, and durability characteristics, along with testing conditions and performance requirements. This connector is designed for applications requiring reliable USB 3.1 Type-C connectivity.

Product Attributes

Brand: Shenzhen Hanxia Electronic Co., Ltd
Part Number: HX USB3.1TYPE-C-16P FS
Material: LCP+30%G.F. UL94V-0
Color: Black
Origin: China
Rating: 20V 5A
Operating Temperature Range: -30C to 80C

Technical Specifications

Item	Test Conditions	Performance/Specification
Mechanical Properties
Connection Force	After connecting and disconnecting using standard plug gauge 3 times.	0.5~2.0Kgf
Disconnect Force	After connecting and disconnecting using standard plug gauge 3 times.	0.6~2.0Kgf
Terminal Strength	Apply a static load of 0.1N/m (1kgf/cm) to the tip of the terminal for 1 min in any direction. There shall be no damage to the terminal such as cracks, looseness or play. Electrical and mechanical characteristics shall be satisfied.	Satisfied
Electrical Properties
Contact Resistance	Measured at small current (100mA or less) at 1000Hz.	40m MAX
Insulation Resistance	Apply a voltage of 100V DC for 1 min to specified portions.	100M MIN
Dielectric Strength	Apply AC 100V rms (50~60Hz) for 1 min with trip current of 0.5mA to specified portions.	Without damage to parts, arcing or breakdown etc.
Durability
Solderability Test	Dip terminal top 1mm in solder bath of 2505 for 50.5 seconds.	Solder wetting time 3 sec; Soldering area 75%
Resistance to Soldering Heat Test (Reflow)	Conditions: Preheat to 180 (120s), Peak temp 2605 ( 20s).	No deformation of case or excessive looseness of terminals. Electrical characteristics satisfied.
Resistance to Soldering Heat Test (Hand Soldering)	Bit temp 3305, application time 30.5 sec. No excessive pressure on terminal.	No deformation of case or excessive looseness of terminals. Electrical characteristics satisfied.
Humidity Test	Store at 402 and 90%-96% RH for 96 Hr, then maintain at standard atmospheric condition for 1 Hr.	No damage on appearance. Mechanical and electrical characteristics satisfied.
Heat Test	Store at 702 for 96 Hours, then recover at room temperature for 1 Hr.	No damage on appearance. Mechanical and electrical characteristics satisfied.
Cold Test	Store at -253 for 96 Hours, then recover at room temperature for 1 Hr.	No damage on appearance. Mechanical and electrical characteristics satisfied.
Life Test (No Load)	10000 cycles (insertion/extraction) at a speed of 10 to 25 cycles/min.	Satisfied
Life Test (With Load)	10000 cycles (insertion/extraction) at a speed of 10 to 20 cycles/min under rating condition (non-inductive load).	Contact Resistance 0.1; Disconnection Force 0.8 to 2.0N; Mechanical and electrical characteristics satisfied.
Temperature Cycling Test	5 cycles of specified temperature conditions, then 30 min room ambient.	No deformation or cracks in molded part. Insertion & Extraction Force: 3 to 20N. Contact Resistance: Max. 30m. Insulation Resistance: Min. 100 M. Dielectric Withstanding Voltage: 100VAC/min (between terminals).
Cold & Heat Shock Test	5 cycles of specified temperature conditions, then 30 min room ambient.	No deformation or cracks in molded part. Insertion & Extraction Force: 3 to 25N. Contact Resistance: Max. 30m. Insulation Resistance: Min. 100 M. Dielectric Withstanding Voltage: 500VAC/min (between terminals).