Vinyl Chloride Acetate Resin With Hydroxyl Group
YD-VROH Vinyl Resin equivalent to VROH
Detailed Product Description Characteristice:A low molecular weight copolymer containing approximately 81 percent vinyl chloride, 4 percent vinyl acetate, and 15 percent hydroxyalkyl acrylate, with the hydroxyl content at 2.0 percent. YD-VROH has excellent adhesion on paper,polysulfone resin,acrylic resin, PVC, ABS, PC and the surface of ink. YD-VROH has good compatibility with other film-forming material, such as alkyd resins, polyurethane elastomers, isocyanate resin,
YD-VAGF Vinyl Resin equivalent to VAGF
Detailed Product Description Characteristice:A high molecular weight copolymer resin containing approximately 81 percent vinyl chloride, 4 percent vinyl acetate, and 15 percent hydroxyalkyl acrylate, with the hydroxyl content at 1.8 percent. VAF has excellent adhesion on paper,polysulfone resin,acrylic resin, PVC, ABS, PC and the surface of ink. YD-VAGF has good compatibility with other film-forming material, such as alkyd resins, polyurethane elastomers, isocyanate resin,
YD-VAGC Vinyl Resin equivalent to VAGC
Detailed Product Description Characteristice:A medium molecular weight copolymer containing approximately 81 percent vinyl chloride, 4 percent vinyl acetate, and 15 percent hydroxyalkyl acrylate, with the hydroxyl content at 1.9 percent. YD-VAGC has excellent adhesion on paper,polysulfone resin,acrylic resin, PVC, ABS, PC and the surface of ink. YD-VAGC has good compatibility with other film-forming material, such as alkyd resins, polyurethane elastomers, isocyanate resin,
YD-VAGD Vinyl Resin equivalent to VAGD/hydroxyl vinyl chloride vinyl acetate
Detailed Product Description Characteristice:A medium molecular weight, partially hydrolyzed vinyl chloride/vinyl acetate resin, made in a two-step precess, having a composition of approximately 90 percent vinyl chloride, 4 percent vinyl acetate, 6 percent vinyl alcohol, with a hydroxyl content of approximately 2.3 percent. YD-VAGD has excellent adhesion on PET, resinprimer, paper, PVC, ABS, pre-treatment of PE and OPP. YD-VAGD has good compatibility with other film-forming
YD-VAGH Vinyl Resin equivalent to VAGH/hydroxyl vinyl chloride vinyl acetate
Detailed Product Description Characteristice:A high molecular weight, partially hydrolyzed vinyl chloride/vinyl acetate resin, made in a two-step process, having a composition of approximately 90 percent vinyl chloride, 4 percent vinyl acetate, 6 percent vinyl alcohol, with a hydroxyl content of approximately 2.3 percent. YD-VAGH has excellent adhesion on PET, resin primer, paper, PVC, ABS, pre-treatment of PE and OPP. YD-VAGH has good compatibility with other film-forming