Zirconia Fused Alumina

Zirconia Fused Alu.oxide #4#5#6#7#8#10#12#14#16#20#24#30#36#46#54#60#70#80#90#100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C

Zirconia Aluminum Oixde #4#5#6#7#8#10#12#14#16#20#24#30#36#46#54#60#70#80#90#100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C Maximum

Zirconia Fused Alumina #4#5#6#7#8#10#12#14#16#20#24#30#36#46#54#60#70#80#90#100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C Maximum

Zirconia Corundum #4#5#6#7#8#10#12#14#16#20#24#30#36#46#54#60#70#80#90#100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C Maximum

Zirconia Corundum F4F5F6F7F8F10F12F14F16F20F22F24F30F36F40F46F54F60F70F80F100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C Maximum

Zirconia aluminum oxide F4F5F6F7F8F10F12F14F16F20F22F24F30F36F40F46F54F60F70F80F100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C

Zirconia fused alu.oxide F4F5F6F7F8F10F12F14F16F20F22F24F30F36F40F46F54F60F70F80F100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C

ZIRCONIA FUSED ALUMINA F4F5F6F7F8F10F12F14F16F20F22F24F30F36F40F46F54F60F70F80F100 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650C Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900C

China manufacturer zicronia alumina F4F5F6F7F8F10F12F14F16F20 Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650℃ Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900℃ Maximum service temperatur

Fused zirconia alumina 0-0.5MM 0.5-1MM 1-1.5MM 1.5-2MM 2-2.5MM 2.5-3MM china manufacturer Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650℃ Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900

Zirconia fused alumina zirconium Corundum ZFA ZA F4-F220 high hardness Chemical Composition(%) Items Al2O3 ZrO2 TiO2 Fe2O3 SiO2 ZA25 68-72 24-30 ≤1.5 ≤0.5 ≤1.0 ZA40 55-57 35-44 ≤1.5 ≤0.5 ≤1.0 Physical Properties Crystal Form Monoclinic,tetragonal system Reaction with acid and alkali no Reaction with carbon Forming carbide since 1650℃ Color Grey True Density 4.20g/cm3 Bulk Density 2.18g/cm3 Moh's hardness 9.0 Knoop hardness 1450-2000kg/cm2 Melting point 1900℃ Maximum service