Fused Spinel

Fused Magnesium Aluminum Spinel 75% Barmac Crushed For Thermal Insulation Materials 1. Fused Spinel Introduction The fused magnesia spinel is made from high-purity light-burned magnesium powder and industrial alumina powder. After smelted by a large high-temperature electric arc furnace, the fused alumina magnesium spinel has the characteristics of high density, good appearance, good corrosion resistance and good thermal shock resistance. It inherits the advantages of high

Fused Magnesium Aluminum Spinel 75% Barmac Crushed For Thermal Insulation Materials 1. Fused Spinel Introduction Our fused aluminum magnesium spinel products include magnesium-rich spinel, general spinel and aluminum-rich spinel. Magnesium-rich spinel is mainly used in cement kiln firing zone with periclase spinel brick, over-spinel brick, lithium battery three-way catalysis sag high resistance in alkaline environment; The general spinel is used for corundum spinel castable

Fused Magnesium Aluminum Spinel 75% Barmac Crushed For Dry Ramming Mass 1. Fused Spinel Introduction Fused Al-Mg spinel quality dry ramming mass is an unshaped refractory material which is prepared by ramming (manual or mechanical) method and hardened by heating at a higher temperature. 2. Fused Spinel Technical specifications Composition Brand AL2O3 MgO CaO SiO2 Fe2O3 Na2O Bulk density(g/cm3) AM-65 64~68 31~36 ≤0.8 ≤0.5 ≤0.6 ≤0.4 ≥3.3 AM-70 71~76 22~27 ≤0.65 ≤0.4 ≤0.4 ≤0.4

Fused Magnesium Aluminum Spinel 75% Barmac Crushed for Refractory Bricks 1. Fused Spinel Introduction A kind of high-purity synthetic refractory raw material made of alumina and high-purity light-burned magnesium as the main raw materials cooling after in an electric arc furnace being melted at a high temperature above 2300°C. 2. Fused Spinel Technical specifications Composition Brand AL2O3 MgO CaO SiO2 Fe2O3 Na2O Bulk density(g/cm3) AM-65 64~68 31~36 ≤0.8 ≤0.5 ≤0.6 ≤0.4 ≥3.3

Fused Magnesium Aluminum Spinel 75% Barmac Crushed for Refractory Materials 1. Fused Spinel Introduction Fused Magnesium Aluminate Spinel manufactured from high purity raw materials in large electric arc furnace. The Fused Spinel supplied by us has high bulk density and good color. It is strong to resist corroding and anti-detonation is better. It dopts high pure MgO and Chemical Al203 to smelt by EAF. Apply to the proof of EAF and basic oxygen furnace steel ladle, intermedia

Fused Magnesium Aluminum Spinel 75% Barmac Crushed For Coatings, Paints, Refractory 1. Fused Spinel Introduction The product is made of Alumina powder and magnesia powder are mixed, smelted in an electric furnace at 2200 degrees Celsius and then screened by crushing. 2. Fused Spinel Technical specifications Composition Brand AL2O3 MgO CaO SiO2 Fe2O3 Na2O Bulk density(g/cm3) AM-65 64~68 31~36 ≤0.8 ≤0.5 ≤0.6 ≤0.4 ≥3.3 AM-70 71~76 22~27 ≤0.65 ≤0.4 ≤0.4 ≤0.4 ≥3.2 AM-85 82~87 12

Quality Magnesium Aluminum Fused Spinel for Refractories Materials 1. Fused Spinel Introduction Fused aluminum-magnesium spinel is smelted by adopting high purity powdered magnesium and powdered commercial alumina through large-scale high-temperature electric arc furnace. It is characterized by high density, good appearance and color, strong corrosion resistance, good thermal shock. It is widely used for refractory products, such as steel-making electric furnace roofs,