Mumetal Permalloy

Mumetal Permalloy Power Wire Coil 1j85 current transformer are general applied in electronic energy meter, power transducer, precision power meter and other power and energy monitoring devices ,over current protection circuit of motor and other electrical appliances . size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

Permalloy Punch Core Application:current transformer Commonly used alloys are 1J50, 1J79, 1J85 and so on. The saturation magnetic induction of 1J50 is slightly lower than that of silicon steel, but its magnetic permeability is dozens of times higher than that of silicon steel, and its iron loss is also 2 to 3 times lower than that of silicon steel. It is made into a transformer with a higher frequency (400~8000Hz), and the no-load current is small. It is suitable for making a

Permalloy core current transformer It is a very widely used soft magnetic alloy. Through appropriate technology, magnetic properties can be effectively controlled, such as initial permeability exceeding 105, maximum permeability exceeding 106, coercivity as low as 2‰ Oersted, rectangular coefficient close to 1 or close to 0, Permalloy with a face-centered cubic crystal structure has good plasticity and can be processed into 1μm ultra-thin ribbons and various forms of use.

Permalloy Punch Core Permalloy often refers to iron-nickel alloys with a nickel content in the range of 30 to 90% size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

Soft Magnetic Alloy Permalloy Core Mu 85 is a soft magnetic nickel-iron alloy with about 80 % nickel, 4.8 - 5.2 % molybdenum, a saturation induction of approx. 0.7 T, the highest technically obtainable permeability, and a very low coercive force. Typical applications are toroidal tape-wound cores, laminations, shieldings, electromagnetic relays. current transformer are general applied in electronic energy meter, power transducer, precision power meter and other power and

Mumetal Permalloy Cut Core Audio Transformer Cores High permeability soft magnetic alloy size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

Permalloy Core 66*18*2MM For Current Transformer 1J85 application range application areas are: 1. Used for core lamination in DC relays, communication and electronic equipment transformers, and chokes 2. Magnetic shielding device, parts or control components size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

66*18*2MM Permalloy Punch Core For Current Transformer Permalloy refers to an iron-nickel alloy with a wide range of nickel content, ranging from 35% to 90%. The biggest feature of Permalloy is its high magnetic permeability in weak magnetic fields. Their saturation magnetic induction intensity is generally between 0.6-1.0T. size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3

66*18*2MM Permalloy Punch Applications: Widely used in radio electronics industry, precision instruments and meters, remote control and automatic control systems. size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

Mumetal Permalloy Cut Core Audio Transformer Cores Applications: Widely used in radio electronics industry, precision instruments and meters, remote control and automatic control systems. size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

1j85 Permalloy Manufacture Mu 85 is a soft magnetic nickel-iron alloy with about 80 % nickel, 4.8 - 5.2 % molybdenum, a saturation induction of approx. 0.7 T, the highest technically obtainable permeability, and a very low coercive force.Typical applications are toroidal tape-wound cores, laminations, shieldings, electromagnetic relays. size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm

Mumetal Permalloy 1j85 Split Cores for Sensor current transformer are general applied in electronic energy meter, power transducer, precision power meter and other power and energy monitoring devices ,over current protection circuit of motor and other electrical appliances . size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

66*18*2MM Permalloy Core Applications: Widely used in radio electronics industry, precision instruments and meters, remote control and automatic control systems. size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

66*18*2MM Permalloy Punch Core For Current Transformer An iron-nickel-based soft magnetic alloy with extremely high magnetic permeability in a weak magnetic field. size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

Permalloy Punch Core Density: 8.75 g/cm3 Melting point: 1395-1425°C 1J85 annealed state, the mechanical properties of the alloy at room temperature: Tensile strength σb (Mpa): ≥560 Elongation rate A5 %: ≥35 Hardness Hv: ≤205 size Input Current Turns ratio Workload Voltage Output Power 66*18*2mm 10A 3500T 3.3K 6.2V 11mW 68*10*2mm 10A 4100T 3.3K 4.5V 6mW 73*10*2mm 10A 4100T 3.3K 4.5V 6mW

Permalloy 1j85 Split Cores for Sensor It is mainly used for power supply, energy conversion, power measurement, leakage protection, etc. For example: various types of current transformers, power transformers, current sensors, etc. used in the power system. It has superior magnetic properties, the highest permeability in the weak magnetic field, the saturation magnetic induction at the bottom and high resistivity, and good consistent performance. It has a wide range of