Carbide Rod With Straight Hole

Cermet Tungsten Carbide Rods with One straight Holes K05-K10 for machining steel ISO K05-K10 Cobalt: 14% Outer diameter 9mm +0.3 Inner diameter: 1.0 +/-0.15 Length: 330mm +3mm Surface roughness: Raw sintered Ra 6.3 or as required Application: particularly for the finish machining of steel. Thanks to its high oxidation resistance and low tendency to stick it is particularly suitable for the production of uncoated reamers. Grade datasheet: ISO CODE U.S.CODE Binder Density

High Kic 13.2 Tungsten carbide straight hole rods OD0.619" Length12.425" ISO K30-K40 Cobalt: 15% Outer diameter 0.619" Inner diameter: 0.079" Length: 12.425" or fixed length as per request Surface roughness: Raw sintered Ra 6.3 or as required Application: with extremely high fracture toughness for particularly unstable and difficult applications. A good choice when switching from HSS to carbide. Grade datasheet: ISO CODE U.S.CODE Binder Density Hardness Transverse KIC g/

0.223" With 12.425" Long Tungsten Carbide Rods Blank W 2 Coolant Holes​ ISO K20-K40 Cobalt: 12% Outer diameter 0.223" Inner diameter: 0.039" Length: 12.425" or fixed length as per request Surface roughness: Raw sintered Ra 6.3 or as required Application: the special high-performance grade for the roughing of titanium and heat-resistant alloys. Grade datasheet: ISO CODE U.S.CODE Binder Density Hardness Transverse KIC g/cm3 HV30 HRA Mpa Mpa.m1/2 K20-K40 C-2 12 14.1 1570 91

Non-alloyed steels cutting blanks tungsten carbide rod with straight hole K20-K40 ISO K30-K40 Cobalt: 10% Outer diameter 10.3mm +0.25-+0.5 Inner diameter: 2mm +/-0.15 Length: 330mm +5 mm or fixed length as per request Surface roughness: Raw sintered Ra 6.3 or as required Application: for universal machining of alloyed and non-alloyed steels. Suitable for a variety of cutting operations on different materials. Improved toughness ensures a low risk of cutting edge breakage

One straight coolant hole carbide rod for making cutting tools for steel stainless steel ISO K20-K40 Cobalt: 9% Outer diameter 2.5-25mm +0.25-+0.5 Inner diameter: as per requested Length: 330mm +5 mm Surface roughness: Raw sintered Ra 6.3 or as required Application: for high-performance machining of steel, stainless steel, and the machining of difficult materials Grade datasheet: ISO CODE U.S.CODE Binder Density Hardness Transverse KIC g/cm3 HV30 HRA Mpa Mpa.m1/2 K20-K40 C-2

Tempered cast iron endmills blank tungsten carbide rods with straight hole ISO K10-K30 Cobalt: 7.5% Outer diameter 6.3mm +0.25 Inner diameter: 1.0mm ±0.15 Length: 210mm +5 mm Surface roughness: Raw sintered Ra 6.3 or as required Application: for machining grey cast iron, tempered cast iron, non-alloyed steel, non-ferrous metals, and plastics Grade datasheet: ISO CODE U.S.CODE Binder Density Hardness Transverse KIC g/cm3 HV30 HRA Mpa Mpa.m1/2 K10-K30 C-3 7.5 14.7 1750 92.8

Diamond coating tungsten carbide rods with straight hole for fiber-reinforced plastics ISO K05-k10 Cobalt: 6% Outer diameter 14.3mm +0.3 Inner diameter: 1.75mm ±0.15 Length: 330mm +5 mm Surface roughness: Raw sintered Ra 6.3 or as required Application: for machining aluminum alloys, fiber-reinforced plastics (carbonfiber and glass-fiber reinforced), composite materials, graphite; particularly suitable for diamond coating Grade datasheet: ISO CODE U.S.CODE Binder Density

OD5mm small tungsten carbide straight hole rods for making drills for HRC 60 steel ISO K10-k20 Cobalt: 12% Outer diameter 5mm +0.3 Inner diameter: 1.5mm ±0.15 Length: 180mm +0.5 mm Surface roughness: Raw sintered Ra 6.3 or as required Application: ultrafine carbide grade for HSC machining of tempered steels up to 60 HRC, suitable for micro-tools and finishing tools and for a variety Recommended Carbide grade ISO CODE U.S.CODE Binder Density Hardness Transverse KIC g/cm3 HV30

HSC machining tempered steel tungsten carbide rods with straight holes KIC 9.2 ISO K10-k20 Cobalt: 8.2% Outer diameter 11mm +0.5 Inner diameter: 1.0mm ±0.15 Length: 120mm +0.5 mm Surface roughness: Raw sintered Ra 6.3 Application: ultrafine carbide grade for HSC machining of tempered steels with a hardness of > 60 HRC and abrasive aluminum alloys Recommended Carbide grade ISO CODE U.S.CODE Binder Density Hardness Transverse KIC g/cm3 HV30 HRA Mpa Mpa.m1/2 K10-K20 C-2 8.2 14

K10 C-2 finished ground tungsten carbide rods with one straight hole with Cobalt 4.2% ISO K05-k10 Cobalt: 4.2% Outer diameter 12mm +0.2/+0.5 Inner diameter: 1.75mm ±0.15 Length: 330mm +3mm Surface roughness: Finished ground Ra0.2 Application: carbide grade with a typical grain size of 0.2 μm for the machining of materials with a hardness > 65 HRC. Thanks to the high wear resistance also excellent suitability for abrasive fiber composite materials. Recommended Carbide grade

Nano Grain size tungsten carbide one straight hole rods for machining stainless steel ISO K05-k10 Cobalt: 9% , other WC 91% Outer diameter 16mm +0.2/+0.5 Inner diameter: 2.0mm ±0.15 Length: 150mm 0/+0.2-0.7mm Surface roughness: Finished ground Ra0.2 Application: Nano grain size, hardness can be up to HV30 1920. used to make drills and end mills for general purpose, such as heat-resistant alloy, cast iron. Recommended Carbide grade Classification K05-K10 Co % 9 WC incl. doping

Cast iron endmills blank OD20mm carbide rods with one coolant hole ISO K10 Cobalt: 7% , other WC 93% Outer diameter 20mm +0.2/+0.5 Inner diameter: 3.0mm ±0.15 Length: 120mm 0/+0.5mm Surface roughness: Raw sintered Application: with a sub-fine grain size of 0.7μm, the hardness could be HV30 1850 and T.R.S 3500, good for making endmills for machining steel, and cast iron. Recommended Carbide grade Classification K10 Co % 7 WC incl. doping 93 Density g/ cm3 14.7 Hardness HV30

Tungsten carbide rods with straight hole for punching pellet mold with hardness HV30 1790 ISO K20 Cobalt: 8% and the rest WC 92% Outer diameter 16mm +0.5 Inner diameter: 10mm ±0.5 Length: 150mm 0/+3mm Surface roughness: Raw sintered Application: Used for making pellet punching rods, with high hardness HV30 1790 and fine grain size. Good wear-resistance performance. Recommended Carbide grade Classification K20 Co % 8 WC incl. doping 92 Density g/ cm3 14.6 Hardness HV30 1790

OD8mm cemented carbide rods with straight hole rods for drilling blanks Specifications: Outer diameter 8mm h6 -0.008 Inner diameter: 1.0mm ±0.15 Length: 330mm 0/+5mm or cut-to-length Surface roughness: Ra 6.3 as Raw sintered Carbide grade datasheet ISO grade K20 Cobalt content: 8% Rest WC 92% Density 14.55g/ cm3 Hardness HV30 1720 Fracture toughness K1c 9.5 Transverse rupture strength 3800 N/mm2 Grain size 0.7μm Regular size for one central hole carbide rods: Outer Diameter

12% Cobalt with high hardness HV1690 tungsten carbide rods with straight hole Outer diameter 12mm +0.3/+0.7 Inner diameter: 1.0mm ±0.15 Length: 330mm 0/+5mm or cut-to-length Surface roughness: Ra 6.3 as Raw sintered Cobalt: 12% ISO K20-K40 Application: Good wear resistance and hardness, it's suitable for machining aluminum alloy. Recommended Carbide grade Classification K20-K30 Co % 12 WC incl. doping 88 Density g/ cm3 14.05 Hardness HV30 1690 Fracture toughness 10.4

OD20mm K20-K40 carbide rods with one central straight hole rod for making endmills Outer diameter 20mm +0.5 Inner diameter: 3.0mm ±0.10 Length: 330mm 0/+5mm Surface roughness: Ra 6.3 as Raw sintered ISO K20-K40 Recommended Carbide grade Classification K20-K40 Co % 10 WC incl. doping 90 Density g/ cm3 14.45 Hardness HV30 1620 Fracture toughness 10.6 Transverse rupture strength 4100 Average grain size 0.6 Regular size for one central hole carbide rods: Outer Diameter mm Inner

Raw Sintered Carbide Rods K15-K20 With Straight Coolant Holes For Steel Machining Outer diameter 6mm +0.5 Inner diameter: 1.0mm ±0.10 Length: 330mm 0/+5mm Surface roughness: Ra 6.3 as Raw sintered ISO K15-K20 Application: High hardness for matching super-hard grey cast steel, hardening steel. Recommended Carbide grade Classification K15-K20 Co % 6 WC incl. doping 94 Density g/ cm3 14.95 Hardness HV30 1620 Fracture toughness 9.9 Transverse rupture strength 3200 Average grain

K20-K40 One central hole carbide rods with straight coolant holes Outer diameter 8mm +0.2/+0.6 Inner diameter: 1.5mm ±0.15 Length: 330mm +5mm Surface roughness: Raw sintered Application: For making endmills or drills Classification K20-K40 Co % 10 WC incl. doping 90 Density g/ cm3 14.5 Hardness HV30 1580 Fracture toughness 11 Transverse rupture strength 4100 Average grain size 0.7 Regular size for one central hole carbide rods: Outer Diameter mm Inner Diameter mm Length mm OD

Unground Two Straight Oil Feed Holes Carbide Rods Fracture toughness 9.5 Cemented Carbide Rods Product details: Diameter: Dia4.3-20.3mm Length: 330mm Material: YL10A Hardness: HRA 92.8 Fracture toughness:10.5 T.R.S :3800 Grain size: Fine 8% Cobalt with fine grain size, high fracture toughness tungsten carbide rods with two straight coolant holes rods. It is recommended for the drilling of cast iron and aluminum alloys. General specifications for the two straight coolant holes