Valox Plastic

S-Plastic Valox 5031resin is a 30% glass reinforced PBT+PC blend with low warpage characteristics. Applications: appliance handles, automotive doorhandles. This grade is a 508 with reduced warpage. ​Property MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 120 MPa ISO 527 Tensile Strain, break, 5 mm/min 2 % ISO 527 Tensile Modulus, 1 mm/min 9000 MPa ISO 527 Flexural Stress, break, 2 mm/min 175 MPa ISO 178 Flexural Modulus, 2 mm/min 8500 MPa ISO 178 Hardness, H358/30

S-Plastic Valox 5021resin is a 20% glass reinforced PBT+PC blend with excellent mechanical and thermal properties. ​Property MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 105 MPa ISO 527 Tensile Strain, break, 5 mm/min 2 % ISO 527 Tensile Modulus, 1 mm/min 7200 MPa ISO 527 Flexural Stress, yield, 2 mm/min 155 MPa ISO 178 Flexural Stress, break, 2 mm/min 160 MPa ISO 178 Flexural Modulus, 2 mm/min 6200 MPa ISO 178 Hardness, H358/30 95 MPa ISO 2039-1 IMPACT Value

S-Plastic Valox V3100HR resin isHydrolytically resistant low viscosity polyester grade. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 55 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 50 % ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 86 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2410 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 1602 J/m ASTM D 4812 Izod Impact, notched, 23°C 53 J/m ASTM D

S-Plastic Valox V3004 resin is Unfilled PBT modified with elastomer. Targeted for flexible hinge, automotive connectors, film applications. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 51 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 22 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 4 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 300 % ASTM D 638 Tensile Modulus, 50 mm/min 2400 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min

S-Plastic Valox IQ315 resin is Environmentally Sustainable Valox iQ315 resin (ASTM datasheet) ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 54 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 33 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 3 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 220 % ASTM D 638 Tensile Modulus, 50 mm/min 2770 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural

S-Plastic Valox V3001MC resin is Unreinforced, directly metallizable PBT injection moulding resin with high flow characteristics ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 55 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 17 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 20 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 100 % ASTM D 638 Tensile Modulus, 50 mm/min 2650 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm

S-Plastic Valox V3000WR resin is Low Friction, Wear resistant PBT ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 50 mm/min 53 MPa ISO 527 Tensile Stress, break, 50 mm/min 50 MPa ISO 527 Tensile Strain, yield, 50 mm/min 6 % ISO 527 Tensile Strain, break, 50 mm/min 20 % ISO 527 Tensile Modulus, 1 mm/min 2500 MPa ISO 527 Flexural Stress, yield, 2 mm/min 70 MPa ISO 178 Flexural Modulus, 2 mm/min 2300 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, notched 80*10*4

S-Plastic Valox 477resin ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 106 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 158 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 7580 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 373 J/m ASTM D 4812 Izod Impact, notched, 23°C 42 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 6.4 mm, unannealed 213 °C ASTM D 648 HDT, 1.82 MPa, 6.4 mm, unannealed

S-Plastic Valox 474resin is 30% GR, UL94V-0/5V rated. Numerous applications; edge trimmers, food mixer motor stator and commutator, cooling fan, connectors,bobbins, switches etc ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 117 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 186 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 7580 MPa ASTM D 790 Hardness, Rockwell R 119 - ASTM D 785 IMPACT Value Unit Standard Izod Impact,

S-Plastic Valox IQ3001 resin is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 56 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 51 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 60 % ASTM D 638 Tensile Modulus, 5 mm/min 2600 MPa ASTM D 638 Flexural Stress, yld,

S-Plastic Valox 471resin is 20% GR PBTP. UL94 V-0/5V rated. Non-blooming flame retardant. ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 96 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 151 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 5510 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 48 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 6.4 mm, unannealed 212 °C ASTM D 648 HDT, 1.82 MPa, 6.4

S-Plastic Valox 470 resin is 7.5% GR PBT, UL94 V-0/5V. ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 79 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 124 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 3510 MPa ASTM D 790 Hardness, Rockwell R 121 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 267 J/m ASTM D 4812 Izod Impact, notched, 23°C 32 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 6.4

S-Plastic Valox IQ2205HV resin is Environmentally sustainable Valox iQ* PBT-ionomer resin for the fibers market. Available in natural color (1001) for use inextrusion/compounding operations. This resin is primarily used as an additive for nylon fibers to enhance cationic dyeability. ​Property PHYSICAL Value Unit Standard Intrinsic Viscosity 0.42 - 0.52 g/dl S-Plastic Method Acid Endgroup Number 50 - 180 meq/kg S-Plastic Method Source GMD, last updated:10/23/2008 Processing Parameter

S-Plastic Valox V3000HR resin is VALOX V3000HR is an unreinforced PBT resin with high viscosity and good hydrolytical stability. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 50 mm/min 55 MPa ISO 527 Tensile Stress, break, 50 mm/min 30 MPa ISO 527 Tensile Strain, yield, 50 mm/min 3.5 % ISO 527 Tensile Strain, break, 50 mm/min 100 % ISO 527 Tensile Modulus, 1 mm/min 2400 MPa ISO 527 Flexural Stress, yield, 2 mm/min 75 MPa ISO 178 Flexural Modulus, 2 mm/min 2300

S-Plastic Valox 469 resin is30% glass filled, flame retardant, utility grade polyester available in black only. ​PropertyMECHANICALValueUnitStandardTensile Stress, yld, Type I, 50 mm/min117MPaASTM D 638Tensile Stress, brk, Type I, 50 mm/min96MPaASTM D 638Tensile Strain, brk, Type I, 50 mm/min3%ASTM D 638Flexural Stress, yld, 1.3 mm/min, 50 mm span175MPaASTM D 790Flexural Modulus, 1.3 mm/min, 50 mm span6890MPaASTM D 790IMPACTValueUnitStandardIzod Impact, notched, 23°C53J/mASTM D

S-Plastic Valox V2015U resin is Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio. ​Property Pr MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 39 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 58 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 17 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 300 % ASTM D

S-Plastic Valox V2000DM resin is Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 59 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 40 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 20 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 100 % ASTM D 638 Tensile Modulus, 5 mm/min 2800 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm

S-Plastic Valox IQ195 resin is Environmentally sustainable Valox iQ195 resin (ASTM datasheet) ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 47 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 47 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 2 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 2 % ASTM D 638 Tensile Modulus, 50 mm/min 2980 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 87 MPa ASTM D 790 Flexural Modulus,

S-Plastic Valox TS4016 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 63 MPa S-Plastic - Japan Method Tensile Strain, break 5 - 5 % S-Plastic - Japan Method Flexural Stress 104 MPa ASTM D 790 Flexural Modulus 4210 MPa ASTM D 790 Hardness, Rockwell R 118 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, notched, 23°C 39 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 189 °C ASTM D 648 HDT, 1.82 MPa, 3.2mm, unannealed 220 °C ASTM D 648

S-Plastic Valox HX420HP resin is Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. Available in limited colors. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 120 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 120 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 3 %