Xenoy Resin

S-Plastic Xenoy 1576VTC resin is a high flow material, for unpainted exterior automotive parts. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Taber Abrasion, CS-17, 1 kg 30 mg/1000cy S-Plastic Method Tensile Stress, yield, 50 mm/min 55 MPa ISO 527 Tensile Stress, break, 50 mm/min 40 MPa ISO 527 Tensile Strain, yield, 50 mm/min 4 % ISO 527 Tensile Strain, break, 50 mm/min >80 % ISO 527 Tensile Modulus, 1 mm/min 2300 MPa ISO 527 Flexural Modulus, 2 mm/min 2100 MPa ISO

S-Plastic Xenoy1403B resin is AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy. Excellent low temperature impact and chemical resistance. Blow Molding grade ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 49 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 47 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 90 % ASTM D 638 Tensile Modulus, 50 mm/min 1930

S-Plastic Xenoy 1402BU resin is Blowmoldable, unreinforced PC+PBT alloy. UV stabilized​PropertyTYPICAL PROPERTIES (1) MECHANICALValueUnitStandardTensile Stress, yld, Type I, 50 mm/min48MPaASTM D 638Flexural Stress, yld, 1.3 mm/min, 50 mm span68MPaASTM D 790Flexural Modulus, 1.3 mm/min, 50 mm span1990MPaASTM D 790IMPACTValueUnitStandardIzod Impact, notched, 23°C694J/mASTM D 256Izod Impact, notched, -30°C534J/mASTM D 256THERMALValueUnitStandardHDT, 1.82 MPa, 6.4 mm, unannealed96

S-Plastic Xenoy 1402B resin is Blowmoldable, unreinforced PC/polyester alloy. Characterized by high melt viscosity/strength with excellent low temperature impact.​PropertyTYPICAL PROPERTIES (1) MECHANICALValueUnitStandardTensile Stress, yld, Type I, 50 mm/min48MPaASTM D 638Flexural Stress, yld, 1.3 mm/min, 50 mm span68MPaASTM D 790Flexural Modulus, 1.3 mm/min, 50 mm span1990MPaASTM D 790IMPACTValueUnitStandardIzod Impact, notched, 23°C694J/mASTM D 256Izod Impact, notched, -30

S-Plastic Xenoy 1333 resin is Unreinforced thermoplastic alloy with excellent chemical resistance and dimensional stability. Cosmetic applications. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 66 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 100 % ASTM D 638 Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790 Hardness, Rockwell R 125 - ASTM D 785 IMPACT Value Unit Standard Izod Impact, notched, 23°C 85 J/m

S-Plastic Xenoy 1200 resin is Unreinforced, opaque, polycarbonate/polyester blend, superior chemical resistance and low temperature impact. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 43 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 175 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 64 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 1790 MPa ASTM D 790 Hardness, Rockwell R 108 - ASTM D 785

S-Plastic Xenoy 1103 resin is AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy. Excellent low temperature impact and chemical resistance. Range gray,black colors. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 51 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 50 MPa ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 150 % ASTM D 638 Tensile Modulus, 50 mm/min

S-Plastic Xenoy 1102 resin is Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 54 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 150 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 82 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 1960 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact,

S-Plastic Xenoy 1101 resin is Unreinforced, opaque polycarbonate/polyester alloy. Excellent low temperature impact plus chemical resistance to automotive fluid. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 52 MPa ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 58 MPa ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 120 % ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 84 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 2040 MPa