Fluoropolymer Resin

PTFE Fine Powder SF-501 with Low RR for Seal Tape, Short Fiber Grades and Technical Properties Item SF-501 SF-503 SF-5046CF SF-504 SF-504X SF-504S Bulk Density, g/L 475±100 Tensile Strength, MPa≥ 24 Elongation, % 480-550 300 250 300 Moisture Content, %≤ 0.03 Standard Specific Gravity ≥ 2.200 2.150-2.200 2.160-2.200 2.150-2.200 2.120-2.150 2.150-2.220 Average Particle Size, μm 400-575 Maximum Reduction Ratio 400:1 Extrusion Pressure, Mpa 20.0-40.0(400:1) 30.0-50.0(400:1) 20.0

PTFE Fine Powder SF-5041 with High RR for Thin Wall Tube and Electric Wire Grades and Technical Properties Item SF-501 SF-503 SF-5046CF SF-504 SF-504X SF-504S Bulk Density, g/L 475±100 Tensile Strength, MPa≥ 24 Elongation, % 480-550 300 250 300 Moisture Content, %≤ 0.03 Standard Specific Gravity ≥ 2.200 2.150-2.200 2.160-2.200 2.150-2.200 2.120-2.150 2.150-2.220 Average Particle Size, μm 400-575 Maximum Reduction Ratio 400:1 Extrusion Pressure, Mpa 20.0-40.0(400:1) 30.0-50.0

PTFE Fine Powder SF-5049 with Medium RR Grades and Technical Properties Item SF-501 SF-503 SF-5046CF SF-504 SF-504X SF-504S Bulk Density, g/L 475±100 Tensile Strength, MPa≥ 24 Elongation, % 480-550 300 250 300 Moisture Content, %≤ 0.03 Standard Specific Gravity ≥ 2.200 2.150-2.200 2.160-2.200 2.150-2.200 2.120-2.150 2.150-2.220 Average Particle Size, μm 400-575 Maximum Reduction Ratio 400:1 Extrusion Pressure, Mpa 20.0-40.0(400:1) 30.0-50.0(400:1) 20.0-35.0(400:1) 30.0-45.0

PVDF Pellet SF-9613 by VDF-HFP Emulsion Polymerization with MFR 9-15 Product Description This grade is prepared by VDF-HFP Emulsion Polymerization. The pellet is well-suited as a good material for jacketing material for both copper and optic fiber applications in the injection or extrusion process. Technical Properties Properties Test Method Unit SF-9613 Composition F-NMR wt% VDF/HFP 10-15 MFR@230℃, 5kg ASTM D1238 g/10min 9-15 Density ASTM D792 g/cm3 1.77-1.78 Melting Point

White and Semi-transparent PVDF Pellet For MoldingProcessing SF-F22M with MFR 1-5 Product Description Polyvinylidene fluoride (PVDF) is the homopolymer of vinylidene fluoride (VDF). It is a new fluorocarbon thermoplastic with excellent mechanical performance, good impact resistance, abrasion resistance, weatherability and chemical stability. It is widely used in chemical industry, electrical and electronic industry, food industry, space industry and architectural decoration

PFA Pellet SF-3104 with MFR 15.1-30 Product Description PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics. Grades and Technical parameters Item SF-3101 SF-3102 SF-3103 SF-3104 Appearance Translucent particles or white powder, no impurities MFR, g/10min 0.8-3.0 3.1-6.0 6.1-15 15.1

PFA Pellet SF-3304B with MFR 16.1-24 Product Description PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics. Grades and Technical Properties Item Unit SF3301 SF3302 SF3303 SF3304 A B C Appearance Translucent particle, without impurities such as metal debris and sand, containing

PVDF Pellet SF-F22FP by VDF suspension for Fishing Line with MFR 1.5-2.5 Product Description This grade is prepared by VDF suspension polymerization. The pellet is well-suited as a good fishing line material. Technical Properties Item unit Test Method SF-F22FP Appearance / 　 White pellet Molecular Weight 　 GPC,DMF 430,000 Intrinsic viscosity Dl/g DMAC 1.25-1.35 MW distribution 　 GPC,DMF 1.8-2.3 MFI@230℃,10Kgs g/10min ASTM D1238 1.5-2.5 Melting point ℃ ASTM D3418 168 Density g

PFA Pellet SF-3102 with MFR 3.1-6.0 Product Description PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics. Grades and Technical parameters Item SF-3101 SF-3102 SF-3103 SF-3104 Appearance Translucent particles or white powder, no impurities MFR, g/10min 0.8-3.0 3.1-6.0 6.1-15 15.1

White and Semi-transparent PVDF Pellet For Injection Processing SF-F22IS with MFR 10-30 Product Description Polyvinylidene fluoride (PVDF) is the homopolymer of vinylidene fluoride (VDF). It is a new fluorocarbon thermoplastic with excellent mechanical performance, good impact resistance, abrasion resistance, weatherability and chemical stability. It is widely used in chemical industry, electrical and electronic industry, food industry, space industry and architectural

PFA Pellet SF-3303 with MFR 6.1-12 Product Description PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics. Grades and Technical Properties Item Unit SF3301 SF3302 SF3303 SF3304 A B C Appearance Translucent particle, without impurities such as metal debris and sand, containing

PFA Pellet SF-3302 with MFR 2.6-6 Product Description PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics. Grades and Technical Properties Item Unit SF3301 SF3302 SF3303 SF3304 A B C Appearance Translucent particle, without impurities such as metal debris and sand, containing

White and Semi-transparent PVDF Pellet For Injection Processing SF-F22IE with MFR 8-26 Product Description Polyvinylidene fluoride (PVDF) is the homopolymer of vinylidene fluoride (VDF). It is a new fluorocarbon thermoplastic with excellent mechanical performance, good impact resistance, abrasion resistance, weatherability and chemical stability. It is widely used in chemical industry, electrical and electronic industry, food industry, space industry and architectural

PVDF Pellet For Color Masterbatch Product Description Designed for fluorine plastic products color matching. Widely used in OK cables, pipes, sheets and plates. Available color: White, Black, Red, Green, Blue, Purple, etc. Tailor-made according to customers’ requirements is also available. Grades and Technical Properties Item Test Method SF-F22MB Color Deviation ISO Grey Scale(1-5) Eyeballing Class one Free of Contamination No black impurity over 200 mesh Yes Bulk Density /g

PVDF Pellet SF-912 PVDF by VDF Emulsion Polymerization with MFR 26-75 Product Description This grade is prepared by VDF Emulsion Polymerization. The pellet is suitable for the injection process. Technical Properties Properties Test Method Unit SF-912 MFR@230℃, 5kg ASTM D1238 g/10min 26-75 Melt Viscosity@230℃,100s-1 ASTM D3853 Ps.s 250-700 Density ASTM D792 g/cm3 1.77-1.78 Melting Point ASTM D3418 ℃ 164-172 Water Absorption ASTM D570 wt% ＜0.05 Tensile @23℃ ASTM D638 　 　

PVDF Pellet SF-916 by VDF Emulsion Polymerization with MFR 8-26 Product Description This grade is prepared by VDF emulsion polymerization. The pellet can be applied in the injection process. Technical Properties Properties Test Method Unit SF-916 MFR@230℃, 5kg ASTM D1238 g/10min 8-26 Melt Viscosity@230℃,100s-1 ASTM D3853 Ps.s 700-1000 Density ASTM D792 g/cm3 1.77-1.78 Melting Point ASTM D3418 ℃ 164-172 Water Absorption ASTM D570 wt% ＜0.05 Tensile @23℃ ASTM D638 　 　 Modulus

PVDF Pellet SF-917 by VDF Emulsion Polymerization with MFR 10-25 Product Description This grade is prepared by VDF emulsion polymerization. The pellet can be applied in the extrusion process. Technical Properties Properties Test Method Unit SF-917 MFR@230℃, 5kg ASTM D1238 g/10min 10-25 Melt Viscosity@230℃,100s-1 ASTM D3853 Ps.s 1600-2200 Density ASTM D792 g/cm3 1.77-1.78 Melting Point ASTM D3418 ℃ 164-172 Water Absorption ASTM D570 wt% ＜0.05 Tensile @23℃ ASTM D638 　 　 Modulus

PVDF Pellet SF-9611 by VDF-HFP Emulsion Polymerization with MFR 3-8 Product Description This grade is prepared by VDF-HFP Emulsion Polymerization. The pellet is well-suited as a good material for jacket applications and heat shrinkable tubes in the injection or extrusion process. Technical Properties Properties Test Method Unit SF-9611 Composition F-NMR wt% VDF/HFP 8-12 MFR@230℃, 5kg ASTM D1238 g/10min 3-8 Density ASTM D792 g/cm3 1.77-1.78 Melting Point ASTM D3418 ℃ 138-142

PFA Pellet SF-3304C with MFR ＞24.1 Product Description PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics. Grades and Technical Properties Item Unit SF3301 SF3302 SF3303 SF3304 A B C Appearance Translucent particle, without impurities such as metal debris and sand, containing

PFA Pellet SF-3103 with MFR 6.1-15 Product Description PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics. Grades and Technical parameters Item SF-3101 SF-3102 SF-3103 SF-3104 Appearance Translucent particles or white powder, no impurities MFR, g/10min 0.8-3.0 3.1-6.0 6.1-15 15.1