FeCrAl Alloy

High Temperature FeCrAl Alloy Heating Wire Kan A1 WireFeCrAl Alloy Electric Heater Wire 0Cr21Al6Nb Product Introduction 0Cr21Al6Nb Wire is a high resistance electric heating alloy wire, the main chemical composition is carbon content ≤0.05%, silicon content ≤0.60%, manganese content ≤0.50%, phosphorus content ≤0.025%, sulfur content ≤0.025%, chromium content 21.0%~23.0%, nickel content ≤0.60%, aluminum content 5.0%~7.0%, niobium content 0.5%, the balance is iron. It has a

0Cr27Al7Mo2 Awg 2 4 6 8 10 12 14 16 18 20 22 24 26 28 30AWG Fecral Alloy Electric Resistance Heating Wire Product Introduction 0Cr27Al7Mo2 Wire is a high resistance electric heating alloy wire, the main chemical composition is carbon content ≤0.05%, silicon content ≤0.40%, manganese content ≤0.20%, phosphorus content ≤0.025%, sulfur content ≤0.020%, chromium content 26.5%~27.8%, nickel content ≤0.60%, aluminum content 6.0%~7.0%, molybdenum content 1.8%~2.2%, the balance is

FeCrAl Round Wire High Temperature 1500℃ Heat Stress-Resistant Wires 0Cr23Al5 Wire Product Introduction 0Cr23Al5 Wire is a high resistance electric heating alloy wire, the main chemical composition is carbon content ≤0.06%, silicon content ≤0.60%, manganese content ≤0.50%, phosphorus content ≤0.025%, sulfur content ≤0.025%, chromium content 20.5%~23.5%, nickel content ≤0.60%, aluminum content 4.2%~5.3%, the balance is iron. It has high resistivity 1.35±0.06μΩ·m (wire diameter

FeCrAl Alloy Customized Bright Resistance Wire 7.35 G/cm3 Density Electric Heat 0Cr21Al6 Wire Product Introduction 0Cr21Al6 Wire is a high resistance electric heating alloy wire, the main chemical composition is carbon content ≤0.06%, silicon content ≤1.00%, manganese content ≤0.70%, phosphorus content ≤0.025%, sulfur content ≤0.025%, chromium content 19.0%~22.0%, nickel content ≤0.60%, aluminum content 5.0%~7.0%, the balance is iron. It has a high resistivity of 1.42±0.07μΩ

FeCrAl Alloy 0Cr25Al5 1.42 Ω/M Resistivity Iron Nickel Cobalt Alloy Wire Product Introduction 0Cr25Al5 Wire is a high resistance electric heating alloy wire, the main chemical composition is carbon content ≤0.06%, silicon content ≤0.60%, manganese content ≤0.70%, phosphorus content ≤0.025%, sulfur content ≤0.020%, chromium content 23.0%~26.0%, nickel content ≤0.60%, aluminum content 4.5%~6.5%, the balance is iron. It has a high resistivity of 1.42±0.07μΩ·m, a density of 7.1 g

Good Corrosion Resistance Heating FeCrAl Electric Resistance Alloy Wire 1Cr13Al4 Wire Product Introduction 1Cr13Al4 Wire is a high resistance electric heating alloy wire, the main chemical composition is carbon content ≤0.12%, silicon content ≤0.7%, manganese content ≤0.5%, phosphorus content ≤0.025%, sulfur content ≤0.02%, chromium content 12.0%~15.0%, nickel content ≤0.6%, aluminum content 4.0%~6.0%, the balance is iron. It has good corrosion resistance and high temperature

Product Description and Application UNS K93600 is also known as 1.3910, Ni36, 1J36 UNS K93600 is new nickel based heat-resistant steel with high hardness, strength and wear resistance. It has good corrosion resistance and oxidation resistance, which is also including good oxidation resistance, high temperature resistance strength (800 ~ 900°C) and toughness. Its good weldability makes it can be hot-rolled or forged at a welding temperature ranging from 300 °C to 600°C, which