Anodized Extruded Aluminium Profiles Industry For Fan Blades
Anodized Extruded Aluminium Profiles Industry For Fan Blades
Descrition:
1. Anodized Extruded Aluminium Profiles Industry For Fan Blades
2. Alloy temper: 6060-T66； 6063-T5/T6 ; 6061-T5/T6 ; 6082-T6; 6005-T6
3. Standard: EN755, ASTMB221, DIN Standard
4. Surface treatment: Mill finish; Anodizing; Powder coated, Brushed.
5. Application: Construction; Car; Aerospace; Ship; Armarium; Industrial equipment; Woodworking machinery and etc.
6. Manufacturing Process: Die designing→ Die making→ Smelting& alloying→ Extruding→ Cutting→ CNC machining→ Driling→ Tapping→ Surface treatment→ Welding→ Assembling→ Packing
Alloy/Temper | 6060-T66； 6063-T5/T6 ; 6061-T5/T6 ; 6082-T6; 6005-T6 |
Surface treatment | Mill finishes; Anodized; Powder coated; Wooden grain, Machine/Acid polished and etc |
Standard apply | EN755; DIN; ASTMB221; GB5237-2008 and etc. |
Price | SMM/LME Primary aluminum price + the most competitive conversion cost |
Mould policy | 100%T/T in advance |
Delivery timetable | sample: within 20 days; order: within 20 days |
Payment term | 30% deposit, the balance pay against B/L copy within 7 days |
Packing standard | Protected film and pearl cotton inside and shrink film outside |
Guarantee term | If the shipped products can not meet required, the total order amount will be refund back without delay, or arrange new replacement cargoes instead. |
Specifications:
1. Primary Technical Data
1) Chemical composition
Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Impurity | Al |
6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | 0.15 | Rest |
6060 | 0.3-0.6 | 0.1-0.3 | 0.1 | 0.1 | 0.35-0.6 | - | 0.15 | 0.1 | 0.15 | Rest |
6005 | 0.6-0.9 | 0.35 | 0.1 | 0.1 | 0.40-0.6 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
2) Mechanical property
Alloy | Temper | Tensile strength | Yield strength | Elongation |
6063 | T5 | ≥ 160Mpa | ≥ 110Mpa | ≥ 8% |
T6 | ≥ 205Mpa | ≥ 180Mpa | ≥ 8% | |
6061 | T6 | ≥ 265Mpa | ≥ 245Mpa | ≥ 8% |
3. Surface Treatment of Sections
| (μm),not diminish than | acid-resistant | abrasion resistance | |||
(Min-average film | (Min-part film | CASS | (S) |
| ||
(h) | Class | (f, g /μm) | ||||
AA10 | 10 | 8 | 16 | ≥9 | ≥50 | ≥300 |
AA15 | 15 | 12 | 32 | ≥9 | ≥75 | ≥300 |
AA20 | 20 | 16 | 56 | ≥9 | ≥100 | ≥300 |
AA25 | 25 | 20 | 72 | ≥9 | ≥125 | ≥300 |
Competitive Advantage:
2.Fair corrosion resistance. Heat treatable
3.Good workability. Good appearance
4.High quality and reasonable price.
5.Our product is your best choice.