6060 Anodized Cnc Machining En755 Heatsink Extrusion Profiles
Anodized Aluminum Heat Sink Extrusion Porifle , With CNC Machining
Description :
1. Description: aluminum extrusion profiles heat sinks from Chinese factory
2. Alloy temper: 6060/6063-T6/T5;
3. Standard: EN755, ASTMB221, DIN Standard
4. Surface treatment: Mill finish; anodized; Powder coated, wooden grain, polished, brushed.
5. Application: Construction; window; door; decoration; Architecture and etc.
6. Advantage:
1) Pure 99.7% aluminum materials without any scrap used
2) OEM welcome, we can design and cut die to meet customer's special demand
3) Wonderful surface treatment, we can meet customers required on surface
4) Strictly quality control process assured higher quality.
5) Packing safety and convenient.
Applications:
Aluminum heat sink is widely used on Machines , cars , lighter ...
Specifications:
1. Primary Technical Data
1)Chemical composition
|
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Impurity |
Al |
|
6063 |
0.2-0.6 |
0.35 |
0.1 |
0.1 |
0.45-0.9 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
|
6061 |
0.4-0.8 |
0.7 |
0.15-0.4 |
0.15 |
0.8-1.2 |
0.04-0.35 |
0.25 |
0.15 |
0.15 |
Rest |
|
6060 |
0.3-0.6 |
0.1-0.3 |
0.1 |
0.1 |
0.35-0.6 |
- |
0.15 |
0.1 |
0.15 |
Rest |
|
6005 |
0.6-0.9 |
0.35 |
0.1 |
0.1 |
0.40-0.6 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
2) Mechanical property
|
Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
|
6063 |
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
|
T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
|
|
6061 |
T6 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8% |
Competitive Advantage:
1, This aluminum extraction profile for heat sink offers excellent engineering design and technical support .
2, With the deep processing ,it will be cut ,punched ,drilled ,milled and then fabricated into the finished product .
3, It is guaranteed on the excellent performance for as long as 15 years .