photovoltaic system power cable 2×6.0mm² (PV1-F / H1Z2Z2-K) Solar Cable

Name: photovoltaic system power cable 2×6.0mm² (PV1-F / H1Z2Z2-K) Solar Cable
Brand: HANGZHOU ZION COMMUNICATION CO., LTD

Price Negotiable

Price: Negotiable

MOQ: 5 KM

Delivery Time: 25 working days

Brand: Zion communication OR OEM

Product Description

2×6.0mm² (PV1-F / H1Z2Z2-K) (NO.7194104)
General characteristics:

Appllcation:
Specifically designed to connect photovoltaic system components inside and outside buildings and facilities under high mechanical demands and extreme weather conditions.
Cable Construction:
Conductor
Metarial:	Tinned annealed copper
Area(mm²) :	2×6.0
Construction(N/mm) :	84/0.30
Conductor(Dia./mm) :	3.17
Insulation	120℃ XLPE
Standard thickness (mm) :	0.75
Standard diameter (mm) :	4.67±0.1
Jacket	120℃ XLPE, Black
Standard thickness (mm) :	1.05
Outer diameter (mm) :	(7.0±0.2)×(14.5±0.2)
Weight rated	102.6
Making	ZION COMMUNICATION PV1-F / H1Z2Z2-K 2x6.0mm² UV Res DC 1.5KV AC 0.6/1KV SOLAR CABLE

Package:
BOX (art.code ZC-100-2×6.0mm/ZC-500-2×6.0mm)
Size: 310x 310x100mm
PALLET (art.code ZC-100-100-2×6.0mm)
Size: 1100x1100mm
Amount of boxes on one pallet:
Weight of total pallet:
Cable length pallet:

Electrical properties
Nominal Voltage:		PV1-F: DC 1.0KV AC 0.6/1.0KV H1Z2Z2-K: DC 1.5KV AC 1.0/1.0KV
Ambient Temperature:		-40℃~+90℃
Max.Temperature at conductor:		+120℃
Service life:		＞25 years ( -40℃~+90℃)
Voltage:		600/1000V
Temperature:		-40~90℃
Conductor resistance (20℃):		3.39Ω/km
Insulation resistance (70℃):		≥1000 MΩ/km
Withstand voltage(V/5min)		AC6500
Speak voltage(V/5min)		AC6500
Min bending radius(mm)		4*D

Main performance parameter of finished cable
Voltage test of finished cable
Min.time of dipping in water			≥1(h)
Testing voltage (AC)			6500(V)
Min.voltage applying time at one time			5(min)
Test result			no breakdown
Sheated surface resistance
Length of specimen:			250mm
Test result			≥109Ω
Penetrate the insulation resistance
Temperature			20℃
Test result			≥1014Ω
High temperature stress
Temperature			140℃
A: with 1.2 Voltage test			A: No breakdown
B: deep pressure			B: Wall thickness 50%
Damp-heat test
Temperature			90℃
Humidity			0.85
Aging before and after the tenslle strength of Change			≤30%
Aging before and after the elongation at break of Change			≤-30%

Acid-alkali Resistance
Min.time of dipping in			168h
Aging before and after the tensile strength of Change			≤-30%
Elongation			≥100
Low-temperature bending
Temperature			-40℃
Time			16h
Test result			No crack
Ozone resistance
Ozeone concentration %			(200±50)x10^-6
Time			72h
Test result			No crack
Heat schrinkable jacket test
Test result			≤2%
Flame retardant-Vertical burn
Flxture on the lower edge from the starting point and carbonization			≥50mm
Burning fuel downward from the lower edge of bottom fixture			≤540mm
Halogen content of non-metallic materials
Test result
Chlorine and bromine content			HCL≤0.5HBr≤0.5%
Fluoride content			F≤0.1%
The inner layer of insulation and sheath of the mechanical properties
Test result
Aging before tensile strength			8.0N/mm²
Aging before elongation			1.25
Aging before and after the tensile strength of change			-30%
Aging before and after the elongation at break of change			-30%
Hot extension
Temperature			200℃
Test result-The inner layer of insulation and sheath
Elongation under load			≤100%
Elongation after unloading			≤25%