Fitness Equipment Epoxy Metal Primer , RAL 1006 Zinc Rich Primer Powder Coating
RAL1006 Maize yellow zinc rich epoxy primer for Fitness Equipment
It is specially designed as a primer in coating systems where extended durability is required.
It provides excellent corrosion protection as part of a complete coating system.
2 component polyamine cured zinc rich epoxy coating. It is a high solids, high zinc dust containing product. The product conforms to the compositional requirements of SSPC paint 20, level 2 and ISO 12944/ISO 20340 and the zinc pigments comply with ASTM D520 type II zinc dust.
POWDER AND COATING PROPERTIES
- Specific gravity : 2.0 - 2.2
- Film thickness (ISO 2178) : 60 - 90 μm
- Flow out : Good
- Gloss (ISO 2813, 60º) : 50-60 %
- Adhesion (ISO 2409) : GT= 0
- Pencil hardness(ASTM D3363 ) : 2H
- Direct and reverse impact (ASTM D2794) : >50kg.cm
- Salt spray Resistance ( ASTM B117, 2000hrs)
- (Maximum undercutting ,2 mm ): No blistering
- Chemical Resistance : Generally excellent resistance to dilute acids, alkalis, oil and most solvents at normal temperatures
Applications of Product
|
Electrical Household Appliances |
Aerospace Area |
|
Automotive Electronics |
Fitness Equipment |
|
Track Traffic |
Medical Devices |
|
Petroleum Pipes, Valve |
Tools & Hardware |
|
LED Lights, Outdoor Lamps |
Radiator & Heat Sink |
|
Glass Decoration |
External Facilities |
Zinc epoxy with zinc silicate properties
New binder technology shows superior performance in adhesion/cohesion and electrical conductivity between the zinc particles and the steel compared to traditional zinc rich epoxy coatings.
Easy application
Fast dry-to-recoat and dry-to-handle
All year around
Can be applied down to 0°C
Surface treatment
New construction: min. Sa 2½ (ISO 8501-1:2007)
Maintenance: UHPWJ to WJ2 (NACE No.5/SSPC-SP 12)
“GreenSteps” – Health, Environment and Safety
High solids and low VOC
Pure zinc dust (ASTM D520 type II)
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.