7049 Forging Aluminum Parts For Aerospace Vehicle Structure Forging Spare Parts OEM
Price:
Negotiations
MOQ:
1PCS
Delivery Time:
15~30days
Brand:
JIMA
Product Description
OEM 7049 Forging Aluminum Parts For Aerospace Vehicle Structure / Forging Metal Parts / Forging Spare Parts
Product Specifications
| Material | Aluminum Alloy 7049 |
| Process | Forging + CNC + Heat Treatment |
| Surface Treatment | Transparent, Color Anodized, Hard Anodizing, Powder Coating; Sandblasting, Laser Carving, Silk Screening; Nickel-Plated, Chrome, Galvanized, Silver/Gold Plating; Black Oxide Coating, Polishing; etc. |
| Manufacture Ability | Depends on the complexity of different products and quantities |
| Experience | Aluminum Machining Service for 12 Years |
| Packaging | Standard Export Wooden Pallets Custom packaging available per customer requirements |
| MOQ | 1 piece |
| Sample | Customizable |
| Mold | Customizable |
| Lead Time | Mold: 15-20 days Process: 15-20 days |
| OEM | Customizable |
Chemical Composition of 7049 Aluminum Alloy
| Element | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others Each | Others Total | Al |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Content (%) | 0.25 max | 0.35 max | 1.20-1.90 | 0.20 max | 2.00-2.90 | 0.10-0.22 | 7.20-8.20 | 0.10 max | 0.05 max | 0.15 max | Rest |
Standard Specifications
- AA 7049-T73
- AA 7049-T735
- UNS A97049
- AA 7049-T73
- AA 7049-T7352
Technical Specifications of 7049-T73
Physical Properties
| Property | Metric | English | Comments |
|---|---|---|---|
| Density | 2.84 g/cc | 0.103 lb/in³ | AA; Typical |
Mechanical Properties
| Property | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 135 | 135 | AA; Typical; 500 g load; 10 mm ball |
| Hardness, Knoop | 170 | 170 | Converted from Brinell Hardness Value |
| Hardness, Rockwell A | 50.5 | 50.5 | Converted from Brinell Hardness Value |
| Hardness, Rockwell B | 82 | 82 | Converted from Brinell Hardness Value |
| Hardness, Vickers | 155 | 155 | Converted from Brinell Hardness Value |
| Tensile Strength, Ultimate | 517 MPa | 75000 psi | AA; Typical |
| Tensile Strength, Yield | 448 MPa | 65000 psi | AA; Typical |
| Elongation at Break | 12% @Diameter 12.7 mm | 12% @Diameter 0.500 in | AA; Typical |
| Modulus of Elasticity | 71.7 GPa | 10400 ksi | AA; Typical; Average of tension and compression |
| Poissons Ratio | 0.33 | 0.33 | |
| Fracture Toughness | 24.0 MPa-m½ (S-L) 34.0 MPa-m½ (L-S) 36.0 MPa-m½ (L-T) |
21.8 ksi-in½ (S-L) 30.9 ksi-in½ (L-S) 32.8 ksi-in½ (L-T) |
K(IC) values in different directions |
| Shear Modulus | 27.6 GPa | 4000 ksi | |
| Shear Strength | 303 MPa | 44000 psi | AA; Typical |
Electrical Properties
| Property | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000432 ohm-cm @20°C | 0.00000432 ohm-cm @68°F | AA; Typical |
Thermal Properties
| Property | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.4 µm/m-°C @20-100°C 25.0 µm/m-°C @20-300°C |
13.0 µin/in-°F @68-212°F 13.9 µin/in-°F @68-572°F |
AA; Typical; average over range |
| Specific Heat Capacity | 0.960 J/g-°C | 0.229 BTU/lb-°F | |
| Thermal Conductivity | 154 W/m-K | 1070 BTU-in/hr-ft²-°F | AA; Typical at 77°F |
| Melting Point | 477 - 635°C | 890 - 1175°F | AA; Typical range |
| Solidus | 477°C | 890°F | AA; Typical |
| Liquidus | 635°C | 1175°F | AA; Typical |
Product Showcase
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JimaFor
Location
No.60 Guoxia Road, Yangpu District, Shanghai,China.
Contact Person
Annie