TA2 Industrial Pure Titanium Rod
High-performance titanium rod specifically engineered for automotive and energy production applications, offering exceptional strength-to-weight ratio and corrosion resistance.
Product Overview
TA2 industrial pure titanium (non-alloyed) provides medium strength with a typical yield strength of 351 MPa. This material features excellent corrosion resistance, superior ductility, and outstanding formability, making it suitable for cold-forming operations and welding applications. The strategic presence of iron and oxygen enhances both strength and formability characteristics.
As a versatile metallic material, TA2 industrial pure titanium is widely preferred in applications requiring significant weight reduction while maintaining structural integrity and strength.
Application Areas
This titanium rod is utilized across multiple high-performance sectors including aerospace, automotive manufacturing, new energy systems, industrial molds and dies, and semiconductor production.
Unique Advantages
- Excellent corrosion resistance
- Superior welding performance
- Excellent formability
- Outstanding strength-to-weight ratio
Main Applications
- Medical components
- Chemical components
- Marine components
- Aerospace components
Execution Standards
- GB/T 2965
Technical Specifications
Chemical Composition (Mass Fraction) / %
| Element | Ti | Fe | C | N | H | O | Other Single | Other Total |
|---|---|---|---|---|---|---|---|---|
| Minimum | Balance | - | - | - | - | - | - | |
| Maximum | Balance | 0.3 | 0.1 | 0.05 | 0.015 | 0.25 | 0.4 |
Mechanical Properties
| Room Temperature Tensile Properties | High Temperature Mechanical Properties | |||
|---|---|---|---|---|
| Property | Minimum | Property | Value | |
| Tensile Strength (Rm) / MPa | 440 | Tensile Strength (Rm) / MPa | -- | |
| Yield Strength (Rp0.2) / MPa | 320 | Test Stress (σ) / MPa | - | |
| Elongation after Fracture (A) / % | 18 | Test Time (t) / h | - | |
| Reduction of Area (Z) / % | 30 | Test Temperature / ℃ | - | |
Product Showcase
Mechanical Properties of Titanium and Titanium Alloy Plates
TA2 Alloy Properties
| Condition | Thickness Range (mm) | Tensile Strength (Rm) / MPa | Yield Strength (Rp0.2) / MPa | Elongation after Fracture /% ≥ | Bending Radius |
|---|---|---|---|---|---|
| M | 0.3 - 1.0 | 440 - 620 | ≥320 | ≥35 | ≥100°, 3t |
| > 1.0 - 2.0 | 440 - 620 | ≥320 | ≥30 | ≥100°, 3t | |
| > 2 - 5.0 | 440 - 620 | ≥320 | ≥25 | ≥90°, 3t | |
| > 5 - 10.0 | 440 - 620 | ≥320 | ≥25 | - | |
| > 10.0 - 30 | 440 - 620 | ≥320 | ≥18 | - |
TC4 Alloy Properties
| Condition | Thickness Range (mm) | Tensile Strength (Rm) / MPa | Yield Strength (Rp0.2) / MPa | Elongation after Fracture /% ≥ | Bending Radius |
|---|---|---|---|---|---|
| M | 0.5 - 1.8 | 925 - 1150 | ≥870 | ≥12 | ≥105°, 9t |
| > 1.8 - 4.0 | 925 - 1150 | ≥870 | ≥12 | ≥105°, 10t | |
| > 4.0 - 5.0 | 925 - 1150 | ≥870 | ≥10 | ≥105°, 10t | |
| > 5.0 - 10.0 | 925 - 1150 | ≥825 | ≥10 | - | |
| > 10.0 - 100 | 925 - 1150 | ≥825 | ≥9 | - |
TC4 High Temperature Properties
| Condition | Thickness Range (mm) | Tensile Strength (Rm) / MPa | Test Temperature (℃) | Test Stress (σ) / MPa | Test Time (t) / h |
|---|---|---|---|---|---|
| M | 0.5 - 30.0 | ≥590 | 400 | 540 | ≥100 |
| M | 0.5 - 30.0 | ≥540 | 500 | 195 | - |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JimaFor
Location
No.60 Guoxia Road, Yangpu District, Shanghai,China.
Contact Person
Annie