TC4 (Ti-6Al-4V) Titanium Alloy Rods and Bars
TC4 (Ti-6Al-4V) is one of the most widely used high-strength titanium alloys, combining excellent corrosion resistance, good mechanical strength and low density (approximately 4.5 kg/dm³).
This heat-treatable titanium alloy can be processed up to 25mm (solution heat treatment + aging) with maximum operating temperatures reaching 400°C. TC4 offers exceptional formability and specific strength, making it the preferred choice for aerospace and motorsports applications, accounting for approximately 50% of global titanium alloy procurement.
Application Areas
Aerospace, automotive and new energy sectors, industrial molds and dies, and semiconductor manufacturing.
Product Specifications
| Unique Advantages | Main Applications | Execution Standards |
|---|---|---|
| Excellent corrosion resistance | Medical components | GB/T 2965 |
| Excellent fatigue strength | Chemical components | GJB 2218A |
| Good machinability | Marine components | GJB 1538A |
| Good strength-to-weight ratio | Racing components | AMS 4928, ASTM B348, AMS-T-9047 |
Chemical Composition
| Element | Ti | Al | V | Fe | C | N | H | O | Other Single | Other Total |
|---|---|---|---|---|---|---|---|---|---|---|
| Min | Balance | 5.5 | 3.5 | - | - | - | - | - | - | - |
| Max | Balance | 6.75 | 4.5 | 0.3 | 0.08 | 0.05 | 0.015 | 0.2 | 0.1 | 0.4 |
Mechanical Properties
Room Temperature Properties
| Property | Minimum Value |
|---|---|
| Tensile Strength (Rm) / MPa | 895 |
| Yield Strength (Rp0.2) / MPa | 827 |
| Elongation after Fracture (A) / % | 10 |
| Reduction of Area (Z) / % | 25 |
High Temperature Properties
| Property | Minimum Value |
|---|---|
| Tensile Strength (Rm) / MPa | 600 |
| Test Stress (σ) / MPa | 560 |
| Test Time (t) / h | 100 |
| Test Temperature / ℃ | 400 |
Product Showcase
Titanium Alloy Plate Mechanical Properties
TA2 Alloy
| Condition | Thickness Range (mm) | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Bending Radius |
|---|---|---|---|---|---|
| M | 0.3 - 1.0 | 440 - 620 | ≥320 | ≥35 | ≥100°, 3t |
| > 1.0 - 2.0 | 440 - 620 | ≥320 | ≥30 | ≥100°, 3t | |
| > 2 - 5.0 | 440 - 620 | ≥320 | ≥25 | ≥90°, 3t | |
| > 5 - 10.0 | 440 - 620 | ≥320 | ≥25 | - | |
| > 10.0 - 30 | 440 - 620 | ≥320 | ≥18 | - |
TC4 Alloy
| Condition | Thickness Range (mm) | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Bending Radius |
|---|---|---|---|---|---|
| M | 0.5 - 1.8 | 925 - 1150 | ≥870 | ≥12 | ≥105°, 9t |
| > 1.8 - 4.0 | 925 - 1150 | ≥870 | ≥12 | ≥105°, 10t | |
| > 4.0 - 5.0 | 925 - 1150 | ≥870 | ≥10 | ≥105°, 10t | |
| > 5.0 - 10.0 | 925 - 1150 | ≥825 | ≥10 | - | |
| > 10.0 - 100 | 925 - 1150 | ≥825 | ≥9 | - |
TC4 High Temperature Performance
| Condition | Thickness Range (mm) | Tensile Strength (MPa) | Test Temperature (°C) | Test Stress (MPa) | Test Time (h) |
|---|---|---|---|---|---|
| M | 0.5 - 30.0 | ≥590 | 400 | 540 | ≥100 |
| M | 0.5 - 30.0 | ≥540 | 500 | 195 | - |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
JimaFor
Location
No.60 Guoxia Road, Yangpu District, Shanghai,China.
Contact Person
Annie