Durable Chrome Plated Steel Bar 42CrMo Hydraulic Cylinder Neutral Salt Spray Test 500 Hours

Price Negotiable

Price: Negotiable

MOQ: 10

Delivery Time: 15-25 days

Brand: DALLAST APT

Product Description

NSS1000 Hours 42CrMo4 Hollow Piston Rod Hard Chrome Plated Steel Bar For Hydraulic Cylinder

CHEMICAL COMPOSITION

Material	C%	Mn%	Si%	S%	P%	V%	Cr%
Ck45	0.42-0.50	0.50-0.80	0.04	0.035	0.035
ST52	0.22	1.6	0.55	0.035	0.04
20MnV6	0.16-0.22	1.30-1.70	0.10-0.50	0.035	0.035	0.10-0.20
42CrMo4	0.38-0.45	0.60-0.90	0.15-0.40	0.03	0.03		0.90-1.20
40Cr	0.37-0.45	0.50-0.80	0.17-0.37				0.80-1.10

Material :45# 42CrMo

Color :Black

NSS:Endure 500 hours

Type:Hollow/Solid Rod

Application Environment:At sea or in harsh environments Surface hardness:＞HV860

SURFACE ROUGHNESS:Ra≤0.2 micron and Rt≤2 micro

TOLERANCES ON DIA:ISO f10 on the diameter

LENGTH:MAX 5 meter

MECHANCIAL PROPERTIES

Material	T.S N/MM2	Y.S N/MM2	E%(MIN)	CHARPY	CONDITION
CK45	610	355	15	>41J	NORMALIZE
CK45	800	630	20	>41J	Q + T
ST52	500	355	22		NORMALIZE
20MnV6	750	590	12	>40J	NORMALIZE
42CrMo4	980	850	14	>47J	Q + T
40Cr	1000	800	10		Q + T

Testing Standing une-en iso9227:2017

· Sal solution: 50 (+/- 5) g/l of NaCl. Water is demineralized and salt purity is 99.5%.

· Environmental temperature: 35 °C.

· pH of salt solution is 6.8.

· Volumen of salt solution is 38.4 ml/day.

· Density of salt solution is 1,030 g/cm3.

· Spraying is 1.5 (+/- 0.5) ml/h.

Test Result :NSS can endure 300 hours ;500 hours; 800 hours

TUV NSS Testing Report SGS NSS Testing Report

Crafts Process Hardening Force Remove

In the whole crafts process, there are 2 times remove hardening forces: the first remove hardening force in the heat treatment process, hardening force remove is about 80%; the second remove hardening force in the surface treatment process, hardening force remove is about 90%-95%. Therefore, the piston rod is not easily deformed during use or transportation.