42CrMo Chrome Plated Steel Bar Hydraulic Cylinder Hollow Piston Neutral Salt Spray Test 500 Hours
42CrMo Hydraulic Cylinder Hollow Piston Rod Hard Chrome Plated Steel Bar Neutral Salt Spray test 500 hours
CHEMICAL COMPOSITION
| Material | C% | Mn% | Si% | S% | P% | V% | Cr% |
| Ck45 | 0.42-0.50 | 0.50-0.80 | 0.04 | 0.035 | 0.035 | ||
| ST52 | 0.22 | 1.6 | 0.55 | 0.035 | 0.04 | ||
| 20MnV6 | 0.16-0.22 | 1.30-1.70 | 0.10-0.50 | 0.035 | 0.035 | 0.10-0.20 | |
| 42CrMo4 | 0.38-0.45 | 0.60-0.90 | 0.15-0.40 | 0.03 | 0.03 | 0.90-1.20 | |
| 40Cr | 0.37-0.45 | 0.50-0.80 | 0.17-0.37 | 0.80-1.10 |
NSS( Salt Spray test )Testing Standing une-en iso9227:2017
· Sal solution: 50 (+/- 5) g/l of NaCl. Water is demineralized and salt purity is 99.5%.
· Environmental temperature: 35 °C.
· pH of salt solution is 6.8.
· Volumen of salt solution is 38.4 ml/day.
· Density of salt solution is 1,030 g/cm3.
· Spraying is 1.5 (+/- 0.5) ml/h.
Test Result :NSS can endure 300 hours ;500 hours; 800 hours
TUV NSS Testing Report SGS NSS Testing Report
Applications:
Single-acting/double-acting hydraulic cylinders --- Garbage trucks, dump trucks, agricultural equipment, ships, mines, drilling platforms, machinery in harsh environments
Detail
| Color | Black |
| Type | Hollow/Solid Rod |
| Application Environment | At sea or in harsh environments |
| Surface hardness | ＞HV860 |
| SURFACE ROUGHNESS | Ra≤0.2 micron and Rt≤2 micro |
| OLERANCES ON DIA | ISO f10 on the diameter |
| LENGTH | MAX 5 meter |
MECHANCIAL PROPERTIES
| Material | T.S N/MM2 | Y.S N/MM2 | E%(MIN) | CHARPY | CONDITION |
| CK45 | 610 | 355 | 15 | >41J | NORMALIZE |
| CK45 | 800 | 630 | 20 | >41J | Q + T |
| ST52 | 500 | 355 | 22 | NORMALIZE | |
| 20MnV6 | 750 | 590 | 12 | >40J | NORMALIZE |
| 42CrMo4 | 980 | 850 | 14 | >47J | Q + T |
| 40Cr | 1000 | 800 | 10 | Q + T |
Crafts Process Hardening Force Remove
In the whole crafts process, there are 2 times remove hardening forces: the first remove hardening force in the heat treatment process, hardening force remove is about 80%; the second remove hardening force in the surface treatment process, hardening force remove is about 90%-95%. Therefore, the piston rod is not easily deformed during use or transportation.