Polished / Wiredrawing Texture Natural Luggage Polycarbonate Film
Price:
Negotiable
MOQ:
50KG
Delivery Time:
14 Work Days
Brand:
DOBESTY
Product Description
DB78DS
Description
PC film is short for Polycarbonate film. It is an amorphous, odorless, non-toxic, highly transparent colorless or slightly yellow thermoplastic engineering plastic.
|
Product Specfication |
|||||
| Code | Color | Texure | Thickness (mm) | Width (mm) | Length(m) |
|
DB78DS Film |
Natural | Polished/ Wiredrawing | 0.2~0.3 | 0~1200 | 500 |
Note:Customizable color can be specified.
Typical Property Values
| Property | Testing Method | Testing Condition | Units | Value |
| Physical | ||||
| Specific Gravity | ISO 1183 | —— | G/cm3 | 1.2 |
| Light Transmission | ASTM D1003 | —— | % | >89 |
| Water Absorption Equilibrium | ASTM D570 | 24 Hours | % | 0.35 |
| Mechanical | ||||
| Tensile Strength | ISO527 | —— | Mpa | 60 |
| Tensile Modulus | ISO527 | Mpa | 2400 | |
| Flexural Modulus | ISO178 | Mpa | 92 | |
| Temperature Resistance | ||||
| Vicat Softening Temperature | ISO306 | ℃ | 148 | |
| Thermal expansivity | ISO11359 | /℃ | 6.5*10-5 | |
| Electrical | ||||
| Permittivity | IEC60250 | —— | 3.1 | |
| Voltage test | IEC60243 | KV/mm | 30 | |
| Volume Resistivity | ICE60093 | 25℃,50%RH | Ω.cm | 1016 |
| Surface Resistivity | ICE60093 | 25℃,50%RH | Ω | 1017 |
| Gaute Variation | >0.5mm ±3% | |||
| 0.25—0.5mm ±5% | ||||
| 0.1—0.25mm ±10% | ||||
| ≤0.1mm ±0.008mm | ||||
Note: The above figures are typical values obtained under standard methods and should not be construed as unsteady application conditions.
Application
Widely used in such as:Luggage bags,school blags,make-up bags,handbags and other fields.The product can be used for high temperature blister molding.
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Kunshan Dobesty Optoelectronic Materials Co.,Ltd
Location
NO.126，Hengchangjing Road ，Zhoushi Town Kunshan City，Jiangsu Province
Contact Person
keron.tang