95WNiFe Tungsten Heavy Alloy Weight For Fishing Use 720-1400 MPa
95WNiFe Good Quality Heavy Tungsten Alloy Weight For Fishing Use
Heavy Tungsten Alloy Weight for Fishing Use is a kind of tungsten base alloy (tungsten content is generally 80% ~ 98%). A small amount of nickel, iron, copper, cobalt, molybdenum, chromium and other elements are added to the alloy material. The density of high specific gravity tungsten alloy can reach 15.20~18.70g/cm3. Tungsten alloy or high density alloy materials can be weighed. Because tungsten alloys weigh more than twice as much as steel.
SPECIFICATION & CHEMICAL COMPOSITIONS (NOMINALS)
| Chemical Composition | 90%W | 93%W | 95%W | 97%W | ||||||
| State | Sinter | Vacuum | Forge | Sinter | Vacuum | Forge | Sinter | Vacuum | Sinter | Vacuum |
| Density (g/cc) |
16.85-17.25 | 17.15-17.85 | 17.75-18.35 | 18.25- 18.85 | ||||||
| Hardness (HRC) |
32 Max | 30 Max | 40 Min | 33 Max | 31 Max | 40 Min | 34 Max | 32 Max | 35 Max | 33 Max |
| Tensile Strength (Max) | 770 Min | 900 Min | 1400 Max |
770 Min | 910 Min | 1440 Max | 735 Min | 920 Min | 700 Min | 850 Min |
| Yield Strength (Mpa) |
620 Min | 620 Min | 1280 Max | 650 Min | 650 Min | 1340 Max | 650 Min | 650 Min | - | - |
| Elongation (%) |
5 Min | 15 Min | 5 Min | 5 Min | 12 Min | 3 Min | 3 Min | 12 Min | 2 Min | 6 Min |
Heavy Tungsten Alloy Weight for Fishing Use Picture:
What is Heavy Tungsten Alloy Weight for Fishing Use?
Tungsten alloy has a series of excellent properties, significant ratio: general 16.5-18.75g/cm3, high strength: tensile strength 700-1000mpa, strong ray absorption capacity: 30-40% higher than lead, high thermal conductivity: 5 is several times that of die steel; Low thermal expansion coefficient: only 1/2-1/3 of steel, good electrical conductivity; Good weldability and machinability.
Common processes for preparing heavy tungsten alloys include mixing the desired amount of tungsten, iron, nickel or copper powder and then cold pressing and liquid phase sintering to near full density. During the liquid phase treatment, the matrix tungsten alloy melts and brings part of tungsten into the solution, forming large tungsten particles (20-60μm) dispersed in the matrix alloy.
Application of Heavy Tungsten Alloy Weight for Fishing Use
Tungsten alloy fishing tackle pendant is a kind of tungsten alloy made of fishing tackle. Tungsten alloy fishing pendant has the advantages of high density, small volume and diverse shapes. Suitable for all river sections. Tungsten alloy hook embodies the advantages different from other manufacturing materials.
- High density: Tungsten alloys have a density of 18.5g/cm3, much less than other materials of the same mass.
- Corrosion resistance: Tungsten alloys have stable chemical properties and will not react with anything at room temperature. If fishing pendants are made of iron, they tend to oxidize after prolonged exposure to water.
- High hardness: Tungsten alloy is second only to diamond in hardness. It is difficult to avoid collision with hard objects during use. The high hardness material makes the fishing pendant resistant to breakage and deformation.