Aluminum Oxide Ceramic High Voltage DC Relay Components
Aluminum Oxide Ceramic Parts for Relay Components
1. Description:
This product is produced with high-purity toughened alumina ceramics and thick-film nickel plating technology. It has high strength and high welding and sealing performance. It is suitable for brazing different materials such as copper and alloys. Reaching the reliable sealing and insulation standards of DC high-voltage relays.
2. Key Words:
HVDC relay, new energy electric vehicle,manufacture samples , open mould ,aluminum oxide,thick-film nickel plating technology,copper and alloys,great limberness,Good corrosion resistance,High intensity,Good high-temperature resistance performance,High purity.
3. Parameters:
| Product Parameters | ||
| Physical Property | Material | 95% Alumina |
| Production Process | Dry Pressing | |
| Product Dimension | Per customers' drawing | |
| Density (g/cm3) | 3.70-3.75g/cm3 | |
| Water Absorption | 0% | |
| Mechanical Performance | Flexural Strength (Mpa) | 310Mpa |
| Modulus of Elasticity (Gpa) | 310Gpa | |
| Hardness (Gpa) | 12.9Gpa | |
| Poisson Ratio | 0.23 | |
| Thermal Character | Linear Thermal Expansion Coefficient | 7.2 |
| Heat Conductivity (W/mk) | 23 | |
| Electrical Property | Dielectric Constant | 9.2 |
| Dielectric Loss Tangent (x10-4) | 8 | |
| Insulation Strength (x106V/M) | 15 | |
| Metalized Ceramic Performance | Air Tightness (Pa·m3/s) | ≤10-8 |
| Bulk Resistivity (Ω·cm) | ≥1010 (20°C), ≥106 (300°C) | |
| Bonding Strength (Mpa) | ≥120Mpa | |
| Metallization Thickness (μm) | ≥20μm | |