Aluminum Oxide Ceramic Structural Parts For HVDC Relay
Aluminum Oxide Ceramic Parts for Relay Components
1. Description:
The new energy series ceramics are produced by high purity complex alumina and nano metallization. It is suitable for brazing of different materials such as copper, aluminum and felling. It is applying to HVDC Relay ,made of 95% aluminum oxide,
2. Key Words:
Relay components, relay ceramic parts, EV vehicles, PHEV vehicles, power charing stations, power storage stations,manufacture samples , open mould ,aluminum oxide,thick-film nickel plating technology,copper and alloys,great limberness,Good corrosion resistance,High intensity,Good high-temperature resistance performance,High purity.
3. Parameters:
| Product Parameters | ||
| Physical Property | Material | 95% Alumina |
| Production Process | Dry Pressing | |
| Product Dimension | Per customers' drawing | |
| Density (g/cm3) | 3.70-3.75g/cm3 | |
| Water Absorption | 0% | |
| Mechanical Performance | Flexural Strength (Mpa) | 310Mpa |
| Modulus of Elasticity (Gpa) | 310Gpa | |
| Hardness (Gpa) | 12.9Gpa | |
| Poisson Ratio | 0.23 | |
| Thermal Character | Linear Thermal Expansion Coefficient | 7.2 |
| Heat Conductivity (W/mk) | 23 | |
| Electrical Property | Dielectric Constant | 9.2 |
| Dielectric Loss Tangent (x10-4) | 8 | |
| Insulation Strength (x106V/M) | 15 | |
| Metalized Ceramic Performance | Air Tightness (Pa·m3/s) | ≤10-8 |
| Bulk Resistivity (Ω·cm) | ≥1010 (20°C), ≥106 (300°C) | |
| Bonding Strength (Mpa) | ≥120Mpa | |
| Metallization Thickness (μm) | ≥20μm | |