High Strength HDPE Film Anti Skid Cross Laminated Film
Anti-skid High Strength HDPE Film Antiskid Cross Laminated Film
Anti-skid High Strength HDPE Film Description:
|
It is a high-strength multi-layer composite film,It is made of HDPE as the base material, adding plasticizer, plasticizer, stabilizer, antioxidant, UV absorber, toughener and other additives through multi-layer co-extrusion blow molding into embryos, and then by multiple pull Stretching, then rotary cutting into a film substrate with a horizontal and vertical distribution of 45 °, and finally through cross-laminated.
It has the thermal stability, dimensional stability, two-way tear resistance, two-way uniform tension and high elongation which are not available in traditional films.
The surface special handling, rough surface, not smooth, make it anti-slip function. Mainly application for self-adhesive membranes, tapes and underlayment for pitched-roof. |
Anti-SKID High Strength HDPE Film Parameter:
| NO. | Item | Performance | ||
| SDM-30 | SDM-60 | |||
| 1 | Tensile Property | Tensile Strength/Mpa ≥ | 30 | 50 |
| MaxF/(N/50mm) ≥ | 200 | 300 | ||
| Elongation as MaxF/% ≥ | 200 | |||
| Elongation at break/% ≥ | 250 | |||
| 2 | Sample number of no broken tested by free-falling dart method ≥ | 8 | ||
| 3 | Tear Strength(Nail Shank)/N ≥ | 60 | ||
| 4 | Angle Tear Strength/N ≥ | 25 | ||
| 5 | Thermal Stability | 120 ℃,10min, No bulb, No deformation | ||
| 6 | Cryogenic Flexibility ℃ |
-35℃, No fissure, No delamination |
||
| 7 | Thermal Ageing | Appearance | No bulb, No deformation | |
| Subsequent MaxF/% ≥ | 80 | |||
| Elongation at MaxF/% ≥ | 200 | |||
| Elongation at break/% ≥ | 200 | |||
| 8 | Artificial Weathering | Appearance | No bulb, No deformation | |
| Subsequent MaxF/% ≥ | 70 | |||
| Elongation at MaxF/% ≥ | 180 | |||
| Elongation at break/% ≥ | 180 |
|||
Anti-slip High Strength HDPE Film Advantages: