High transparency viscosity Liquid Addition Cure Molding Silicone Rubber For Jewelry Molds

Product description of high transparency viscosity liquid addition cure molding silicone rubber for jewelry molds

MC Silicone MCPLA-H40 is a two-component elastomeric material consisting of Silicone Base, which when mixed with Curing Agent,cures to an elastic and resistant material at room temperature by an addition reaction. The curing can be heat accelerated. A range of materials can be cast into the cured silicone mold.

Features of high transparency viscosity liquid addition cure molding silicone rubber for jewelry molds

High Transparency

Good flowability

High tear and tensile strength

Long shelf life with low shrinkage

Fast mixing (10:1)

Flexible and dimensional stability

Applications of high transparency viscosity liquid addition cure molding silicone rubber for jewelry molds

Label manufacturing, hearing aid earmold, molding applications requiring low shrinkage e.g., jewelry, automotive. It can be used to make exceptionally strong and tear resistant molds for casting wax, resins and other materials, etc.

Technical Properties of high transparency viscosity liquid addition cure molding silicone rubber for jewelry molds

Processing and Instructions

1. Mixing the two components

According the mixing ration 10:1 weighting A and B, the two components may be thoroughly mixed either by hand or using a low-speed electric to minimize the degassing

of bubbles and to avoid any temperature increase. Note: It is also possible to use a special mixing and dispensing machine for the silicone components, further information is available upon request.

2. Moulding

The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3-4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.

Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter/height ratio (3 to 4 times of the initial volume)

3. Polymerisation

The curing may be slowed down at lower temperature or accelerated by applying heat.

Note: in general contact with certain materials can inhibit the cross linking of RTV.

 Natural rubbers vulcanized with sulfur

 RTV silicone compound catalyzed with metal salts, e.g. Tin compounds

 PVC stabilized with tin salts and additives

 Epoxy catalyzed with amines

 Certain organic solvents, e.g. Ketones, alcohols, etc.

In case of doubt, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.

Packaging of high transparency viscosity liquid addition cure molding silicone rubber for jewelry molds

Part A: 20kg per drum, Part B: 1kg per bottle

Special containers are available are on request.

Storage and shelf life of high transparency viscosity liquid addition cure molding silicone rubber for jewelry molds

MC Silicone has a usable life of 12 months from the date of production with the original package stored at a temperature below 25°C. Use the product as soon as the packaging has been opened.