Tin Cure Silicone Rubber with High Tear Strenth for Sculptures

DESCRIPATION of Tin Cure Silicone Rubber with High Tear Strenth for Sculptures

Silicone rubber MCSIL-2020 is a two-component material, consisting of Part A Silicone base and Part B curing agent, cures at room temperature by a condensation reaction.

APPLICATIONS of Tin Cure Silicone Rubber with High Tear Strenth for Sculptures

MC RTV-2 mold making silicone rubber are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds, etc.

FEATURES of Tin Cure Silicone Rubber with High Tear Strenth for Sculptures

• Good flow ability and long working time
• Medium hardness
• High tear and tensile strength
• Easy de-mould from complex replica parts
• Acid and alkali-resistance
• Low linear shrinkage

Tin series good for pouring mold making

Silicone Base and Curing Agent Mixture (100:2 by weight) in 25 C (77F) testing

How to make the silicone mold?

• The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
• Mixing

Please weight 100 Part A base and 2 parts of Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the curing agent completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent.

It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Pouring the mixture and curing

Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

• STORAGE of Tin Cure Silicone Rubber with High Tear Strenth for Sculptures

When stored at or below 30 C (85F) in the original unopened containers, silicone base and [art B curing agent have a usable life of 12 months from the date of production. After 12 months stock, please use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again, no influence for other performances.

• Packing of Tin Cure Silicone Rubber with High Tear Strenth for Sculptures

silicone rubber Part A: 1kg=504kg pallet, 5kg/drum=600kg/pallet, 10kg, 20kg per plastic drum=480kg per pallet
200kg per drum, 800kg per pallet. Other types of package, please check with our sales representative.
silicone rubber Part B: 0.8kg/bottle, 1kg/bottle.

• Note:

Silicone MCSIL series is an industrial product and must not be used in food contact and dental human skin molding applications.