YG8 Aluminum K30 Carbide Milling Inserts HRA 92.5 OD 42mm ID 12mm
YG8 Aluminum Milling Inserts K30 Carbide Metal Cutting Tools
Special Alu milling tools. Customized by the customer for milling aluminum material. The milling inserts requests high hardness and wear-resistance performance, and OED recommended K30(YG8) as material for these inserts.
Testing report:
Compare to the previous milling insert 3,000pcs, OED milling tools worked for machining 5,500pcs. The service life has been increased almost 80%.
Main dimension:
OD 42mm
ID 12mm
Thickness 12mm
Ground surface, roughness Ra 0.8
Recommended grades for metalworking
| Application Code |
Chemical Composition | Physical Properties of powder |
Physical and mechanical properties and micro structure as sintered |
Application recommended | ||||||||
| Co | Tic/ TacNbc |
WC | Hall Flow | Apparent density |
Density | Hardness | Transverse rupture strength |
Coercivity | Magnetic saturation |
Porosity | ||
| s/25cm3 | g/cm3 | g/cm3 | HV 30 | N/mm2 | KA/m | % | ||||||
| P10 | 9.5 | 35 | 55.5 | 35 | 2.52 | 10.3 | 1525-1675 | ≥1130 | 9.2-11.5 | 8.3-9.5 | A02 B00 | For machining steel and cast steel |
| P20 | 8.2 | 14 | 77.8 | 32 | 2.83 | 11.52 | 1560-1700 | ≥1400 | 12.0-15.5 | 7.5-8.2 | A02 B00 | For machining long-chip steel, cast steel and forgeable cast iron |
| P25 | 9.5 | 21.9 | 68.6 | 35 | 2.5 | 11.42 | 1400-1550 | ≥1700 | 8.0-10.4 | 8.5-9.5 | A02 B00 | |
| P30 | 9.3 | 6.3 | 84.4 | 32 | 3.14 | 13.02 | 1370-1560 | ≥1750 | 9.5-12.5 | 8.6-9.2 | A02 B00 | |
| 10 | 20 | 70 | 33 | 3.08 | 12.86 | 1425-1575 | ≥1600 | 13.7-15.5 | 8.1-9.1 | A02 B00 | ||
| P35 | 11 | 12 | 77 | 35 | 3.24 | 13.12 | 1320-1460 | ≥1650 | 10.7-13.1 | 9.1-10.1 | A02 B00 | For machining steel and cast steel parts with different pores including sand holes. |
| P40 | 12 | 18.93 | 69.07 | 35 | 2.88 | 12.75 | ≥1400 | ≥2250 | 15.0-19.0 | 10.0-11.2 | A04 B02 | |
Our advantages:
- CIP forming.
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
- Cryogenic process
The internal stress can be removed through the cryogenic process to improve the microstructure.
- Vibration process
The internal stress can be removed through the vibration process to improve the overall performance.
- Heat treatment
The service can be improved through the heat treatment process.
Why choose us for carbide wear parts:
- Professional production equipment. From spray drying towers, extrusion molding, mold molding, injection molding, CIP, HIP sintering furnaces, flat grinders, heartless grinders, round grinders, EMD cutting, polishing machines, etc. OED can provide reliable quality assurance for your products.
- The strict control of the production processing. From raw materials, sintering, processing, we will strictly test each process, non-conforming products will not enter the subsequent production.
- Proficient technical team. Senior carbide raw materials engineers: To analyze whether the product meets your application requirements. Senior production managers: To study the most suitable for your product processing methods. Skilled technical inspectors: To test whether the finished product meets your drawing requirements.
- Reliable service. Not only can we provide pre-sales technical services, but our engineers can also come up with product improvements to provide the most reasonable solution for your product.
- Low-cost sample development. For trial orders, such as quantity below 10pcs, our engineer team can help customers to find the solution with mold fees. In this way, our customers can try the samples at a minimized cost.
- Fast delivery. Standard products could be delivered in one week, and the special carbide tools could be finished in 25-45 days after confirming the drawings or 3D model.