Customized Vacuum Calcium Silicate Board Production Line
Calcium Silicate Board Production Line
2020-03-28 10:23:30 105
beatingpaper pulp treatment systemback to water tankcontrol room vacuum system breaking machinethickness counterCopy system board hostProduct specification :L×W×T:2440 ×1220×6mm~20mmProduct with special
- Introduction
- Requirement
- Other
|
beating |
paper pulp treatment system |
|
back to water tank |
control room |
|
vacuum system |
breaking machine |
|
thickness counter |
Copy system board host |
Product specification :
-
L×W×T:2440 ×1220×6mm~20mm
-
Product with special specification can also be produced as per requirement of the
customer
Quality Standard
For main technical performance index please see the following table:
|
Item |
Unit |
Calcium Silicate Board |
|
Density |
g/cm3 |
0.9-1.40 |
|
Flexural Strength |
MPa |
＞9 |
|
Heat Conductivity |
w/m.k |
＜0.29 |
|
Impact Strength |
kJ/mm2 |
＞2.0 |
|
Withdrawal Force Of Screw |
N/mm |
＜0.2 |
|
Drying Shrinkage |
% |
Fit Grade Anon-inflammable materialinGB862(China National) Standard) |
|
Non-inflammability |
Other:
Theoretical Capacity:10000 /day
Pre-curing Time :8h
Daily Productive Time:22h
Quantity of Autoclave:2
Specification of Autoclave :2X26m
Running Time of Autoclave : 24hours
Uninterrupted Curing
Auto claving Period:
16 hours in average(This period was made according to appraisement of similar plant,
The specific period will be ensured through test in laboratory after raw materials
confirmed. )
Reserve of main raw material:
Dosage of fiber material should last 7 days.Dosage of powdery material such as cement,quartz powder should last for 3 days.
More detail should be further discussed.
Basic requirement for quality of raw material :
Quartz sand:SiO2 ≥95% Fineness:residueon200poresieve ＜10%
Cement:ordinary Portland cement with gradeofabove42.5.
slaked lime powder :
CaO+MgO ≥75%