C22E W-Nr 1.1151 Structural Steel Plates UNS G10200 C20E4 S20C Metal Flat Plate
C22E W-Nr 1.1151 Structural Steel Plates UNS G10200 C20E4 S20C Metal Flat Plate
Describe
1.1151 flat steel is a high-quality quenched and tempered carbon structural steel, which belongs to high-quality low-carbon, low-carbon chromium, molybdenum, nickel surface hardened steel. DIN 1.1151 Steel Annealed delivery hardness less than 250HB. 1.1151 has a moderate carbon content range.
Size Range
| Round bar / Wire rod (Diameter) | 5.5mm to 800mm |
| Square bar / Flat bar | 3mm to 800mm |
| Forging piece | Stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM. |
| Heavy/middle plate via hot rolled | T6 - 200mm X W10 - 1500mm X L1000-12000mm |
| Sheet steel via cold rolled: | T0.5 - 4mm X W6 - 1000mm X L1000 - 1000mm |
| Steel strip via cold rolled: | T0.1 - 3.0mm X W5 - 190mm X L (or in coil form) |
| Length | Fixed length or random length or based on the customer's special requirement. |
Chemical Composition and standard
| Grade |
C22E/W-Nr 1.2360 |
BS C22E/NF C22E | 1020/G10200 |
| Standard | DIN EN 10083-2(2006) |
NF EN 10083-2(2006)/ BS EN 10083-2(2006) |
ASTM A29 / A29M(2005) |
| Chemical Composition (weight%) |
C(％): 0.17~0.24 Si(％): ≤0.40 Mn(％): 0.40~0.70 S(％)≤: 0.035 Ni(％): ≤0.040 |
C(％): 0.17~0.24 Si(％): ≤0.40 Mn(％): 0.40~0.70 S(％)≤: 0.035 Ni(％): ≤0.040 |
C(％): 0.18~0.23 Si(％): 0.20~0.40 Mn(％): 0.30~0.60 S(％)≤: 0.050 Ni(％): -- Cu(%): ≤0.20 |
| Grade | JIS S20C | ISO C20E4 | KS SM20C |
| Standard | JIS G4051(2005) | ISO 683 / 19(1996) | KS D3752(2007) |
| Chemical Composition (weight%) |
C(％): 0.18~0.23 Si(％): 0.15~0.35 Mn(％): 0.30~0.60 S(％)≤: 0.035 Ni(％): ≤0.020 Cu(%): ≤0.30 |
C(％): 0.17~0.23 Si(％): 0.10~0.40 Mn(％): 0.30~0.60 S(％)≤: 0.035 Ni(％): -- |
C(％): 0.18~0.23 Si(％): 0.15~0.35 Mn(％): 0.30~0.60 S(％)≤: 0.035 Ni(％): ≤0.020 Cu(%): ≤0.25 |
Mechanical Properties
C22E/1.1151 Structural Steel Mechanical Properties
| Tensile strength,Rm/MPa: | ≥600 |
| Yield strength,Rp/MPa: | ≥355 |
| Elongation/%: | ≥16 |
| Reduction of area, ψ/%: | ≥40 |
| Impact, KV /J: | ≥39 |
| Hardness/HB: |
no heat treatment, ≤229HB annealed steel, ≤197HB |
Applications
Forming dies, stamping dies, die inserts, extrusion dies, cold extrusion tools, pipe tools, blanking tools, stamping tools, embossing tools, cutting tools, industrial tools, wood chip cutting tools, veneer tools, reinforcements.