China X80CrNiSi20 W-Nr 1.4747 Steel Forging Parts UNS S65006 AISI HNV6 SUH4 Cold Rolled Strip for sale

X80CrNiSi20 W-Nr 1.4747 Steel Forging Parts UNS S65006 AISI HNV6 SUH4 Cold Rolled Strip

Name: X80CrNiSi20 W-Nr 1.4747 Steel Forging Parts UNS S65006 AISI HNV6 SUH4 Cold Rolled Strip
Brand: Mianyang Baoheng New Material Technology Co.,Ltd

Price Negotiable

Price: Negotiations

MOQ: 800kg

Delivery Time: Ex-stock for delivery: 3-7 days Production lead time: 30-60 days

Brand: PANGANGGROUP,TISCO,ANSTEEL,BAOSTEEL

Product Description

X80CrNiSi20 W-Nr 1.4747 Steel Forging Parts UNS S65006 AISI HNV6 SUH4 Cold Rolled Strip

Size Range

Round bar / Wire rod (Diameter):	5.0 mm to 1000 mm
Square bar / Flat bar:	7.0 mm to 1000 mm
Forging piece:	Stepped shafts with flanks/discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Heavy/middle plate via hot rolled:	T5 - 500 mm X W5 - 1000 mm X L1000-10000 mm
Sheet steel via cold rolled:	T0.7 - 10.0 mm X W5 - 1000 mm X L1000 - 10000 mm
Steel strip via cold rolled:	T0.7 - 10.0 mm X W5 - 1000 mm X L (or in coil form)
Length	Fixed length or random length or based on the customer's special requirement.

Chemical Composition and standard

HNV6/S65006	X80CrNiSi20/1.4747	SUH 4 / STR 4
SAE J775(1993) / UNS(2004)	--	JIS G 4311(1991) / KS D3731(2007)
C(％): 0.75~0.85 Si(％): 1.75~2.50 Mn(％): ≤0.80 P(％)≤: 0.040 S(％)≤: 0.030 Cr(％): 19.0~21.0 Ni(％): 1.00~1.70 Mo(％): --	C(％): 0.75~0.85 Si(％): 1.75~2.75 Mn(％): ≤1.00 P(％)≤: 0.030 S(％)≤: 0.030 Cr(％): 19.0~21.0 Ni(％): 1.00~1.75 Mo(％): --	C(％): 0.75~0.85 Si(％): 1.75~2.25 Mn(％): 0.20~0.60 P(％)≤: 0.030 S(％)≤: 0.030 Cr(％): 19.0~20.5 Ni(％): 1.15~1.65 Mo(％): --
Z80CSN20-02	443S65
NF A35-579(1991)	BS 970-4(1996)
C(％): 0.75~0.85 Si(％): 1.75~2.50 Mn(％): ≤0.80 P(％)≤: 0.040 S(％)≤: 0.030 Cr(％): 19.0~21.0 Ni(％): 1.00~1.70 Mo(％): --	C(％): 0.75~0.85 Si(％): 1.75~2.2.25 Mn(％): 0.30~0.75 P(％)≤: 0.040 S(％)≤: 0.030 Cr(％): 19.0~21.0 Ni(％): 1.20~1.70 Mo(％): -- Pb(%): ≤0.15

Mechanical Properties

HNV6/S65006 Steel Forging Parts Mechanical Properties

Tensile strength, Rm/MPa:	≥ 671
Yield strength, Rp/MPa:	≥ 727
Elongation/%:	13
Reduction of area, ψ/%:	22
Impact, KV /J:	32
Annealed hardness HBW:	221