AMS 5629 Metal Flat Bar
AMS 5629 Turbine Blade Steel AMS 5629 Round Bar AMS 5629 Flat Bar AMS 5629 Bar
Description
Our company provides AMS 5629 Turbine Blade Steel AMS 5629 Hot rolled round bars Hot rolled flat bars.
All of PH13-8Mo Turbine Blade Steel XM-13 Round Bar AMS 5629 Flat Bar UNS S13800 Bar 1.4534 13-8Mo conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
- Material:Metal,Turbine Blade Steel.AMS 5629 Turbine Blade Steel AMS 5629 Hot rolled round bars Hot rolled flat bars.
- Round bar / Wire rod (Diameter): 5.5mm to 800mm
- Length: Fixed length or random length or based on the customer's special requirement.
Products Details
AMS 5629 Turbine Blade Steel AMS 5629 Hot rolled round bars Hot rolled flat bars.
| Chemical Composition (weight%): | C (％): ≤ 0.05 |
| Si (％): ≤ 0.10 | |
| Mn (％): ≤ 0.20 | |
| P (％)≤: 0.010 | |
| S (％)≤: 0.008 | |
| Cr (％): 12.3 ~ 13.2 | |
| Ni (％): 7.50 ~ 8.50 | |
| Mo (％): 2.00 ~ 2.50 | |
| Al (％): 0.90 ~ 1.35 | |
| N (%): ≤ 0.01 | |
| Mechanical Properties Under Final Heat Treatment: |
Solution treatment temperature and cooling ways: 1050 +/-15℃ |
| Ageing teated: H1000, 540℃, 4h, air cooling | |
| Tensile strength, σb≥/MPa: 1410 | |
| Yield strength, σ0.2≥/MPa: 1312 | |
| Elongation, δ≥(％): 10.0 | |
| Hardness |HRC: 43 | |
| Ageing teated: H1025, 550℃, 4h, air cooling | |
| Tensile strength, σb≥/MPa: 1275 | |
| Yield strength, σ0.2≥/MPa: 1200 | |
| Elongation, δ≥(％): 11.0 | |
| Hardness |HRC: 41 | |
| Ageing teated: H1050, 565℃, 4h, air cooling | |
| Tensile strength, σb≥/MPa: 1200 | |
| Yield strength, σ0.2≥/MPa: 1135 | |
| Elongation, δ≥(％): 12.0 | |
| Hardness |HRC: 40 | |
| Ageing teated: H1100, 595℃, 4h, air cooling | |
| Tensile strength, σb≥/MPa: 1030 | |
| Yield strength, σ0.2≥/MPa: 930 | |
| Elongation, δ≥(％): 14.0 | |
| Hardness |HRC: 34 | |
| Ageing teated: H1150, 620℃, 4h, air cooling | |
| Tensile strength, σb≥/MPa: 930 | |
| Yield strength, σ0.2≥/MPa: 625 | |
| Elongation, δ≥(％): 14.0 | |
| Hardness |HRC: 30 |
Applications:
AMS 5629 is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
AMS 5629 Turbine Blade Steel AMS 5629 Round Bar AMS 5629 Flat Bar AMS 5629 Bar
FAQ
Q: How do you control the quality?
A: We have professional inspectors to analyze the chemical composition of AMS 5629 Turbine Blade Steel AMS 5629 Round Bar AMS 5629 Flat Bar AMS 5629 Bar and test the finished products in strict accordance with the standards stipulated in the contract. In this process, the inner and outer surfaces, the appearance of both ends, bending, set length, outer diameter and Wall thickness will be checked one by one. You can rest assured that all products you receive from us are reliable.
Q: Do you accept customization?
A: Yes. If you have special requirements for products or packaging, we can make them for you.
Q: Can you accept trial orders?
A: Our MOQ is usually 1 ton. However, if you want to place an order as the start of our cooperation, we can accept smaller quantities at the first time. Of course, after the start, we will have further and longer cooperation.
Q: How do I get samples?
A: Free samples are available for your inspection and testing, DHL/FedEx/UPS accounts can be used for sampling, and the courier fee is borne by you.
Submit an enquiry for the displaying steel materials you are interested in TODAY!
Sales Engineer: sales@ss-bars.com
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.