5.5mm 6.5mm Carbon Steel Wire Coils SAE 1006 1008 1008B Hot Rolled Rod

SAE 1006 (according to ASTM A510M) steel is commonly used in manufacturing rolled wire with subsequent drawing and no prior or subsequent heat-treatment. Its chemical composition allows for a high level of zinc adhesion to the steel base and provides ideal conditions for the production of galvanized and rolled wire.

Weldable steel wire in coils for thin drawing. Material according to ISO 16120- 2 C4D, ASTM A510M - SAE1006 and EN 10025-2 S235JR standards.

GRADE

EQUIVALENT GRADE OF SAE 1006

CHEMICAL COMPOSITION

MECHANICAL AND DIMENSIONAL PROPERTIES

Tensile Strength : 380<Rm[MPa]≤420

Yield Strength : ReMPa]≥235

Elongation : A10[%]≥30

Elongation : A5[%]≥32

Diameter : 5.5mm~20mm

Diameter Tolerance and out-of -round : According to ASTM510M

WELDING

SAE 1006 low-carbon structural steel is ductile and not prone to brittleness or fragility. Any convenient welding method can be used: argon-arc non-consumable electrode, manual continuous electrode, and submerged argon-arc electrode with protection. Preheating and subsequent heat-treatment are not necessary.

SURFACE AND INTERNAL QUALITY

Surface quality: according to ISO 16120-2 par. 4.3 and 4.4 – maximum defect depth 0,20 mm.
Internal quality: absence of defects compromising use (ISO 16120-2 par. 4.5).

STANDARD PACKING

In coils up to approx. 2500 kg, inside diameter about 800 mm, outside diameter about 1200 mm, maximum length 1900 mm.

STANDARD CERTIFICATION

On demand Inspection Certificate according to EN 10204 3.1 and for diameter range 5,5 ÷ 13 mm the Declaration of Performance according to CPR (Reg UE 305/2011).