S-Plastic Xylex EXXY0009 Unreinforced, PC+Polyester Alloy With High Heat Properties For Extrusion Applications.

Name: S-Plastic Xylex EXXY0009 Unreinforced, PC+Polyester Alloy With High Heat Properties For Extrusion Applications.
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Xylex

Product Description

S-Plastics Xylex EXXY0009 resin is WILL BE COMMERCIALIZED AS X7001EX. Unreinforced, PC+polyester alloy with high heat properties for extrusion applications.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 50 mm/min	55	MPa	ISO 527
Tensile Stress, break, 50 mm/min	57	MPa	ISO 527
Tensile Strain, break, 50 mm/min	>150	%	ISO 527
Tensile Modulus, 1 mm/min	2000	MPa	ISO 527
Flexural Stress, break, 2 mm/min	72	MPa	ISO 178
Flexural Modulus, 2 mm/min	2100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	10	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -10°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	121	°C	ASTM D 1525
Thermal Conductivity	0.23	W/m-°C	ISO 8302
CTE, 23°C to 60°C, flow	8.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	8.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/120	121	°C	ISO 306
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	105	°C	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Melt Flow Rate, 265°C/2.16kg	9	g/10 min	ASTM D 1238
Density	1.18	g/cm³	ISO 1183
Melt Volume Rate, MVR at 265°C/2.16 kg	8	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/1.2 kg	13	cm³/10 min	ISO 1133
Source GMD, last updated:06/18/2001