S-Plastic Thermocomp MX06402H is based on Polypropylene base resin containing glass fiber. Characteristics of this grade a

Name: S-Plastic Thermocomp MX06402H is based on Polypropylene base resin containing glass fiber. Characteristics of this grade a
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp MX06402H resin is based on Polypropylene base resin containing glass fiber. Characteristics of this grade are Heat

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	38	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	34	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	3.4	%	ASTM D 638
Tensile Modulus, 50 mm/min	6390	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	66	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	4700	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	37	MPa	ISO 527
Tensile Stress, break, 5 mm/min	35	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.7	%	ISO 527
Tensile Strain, break, 5 mm/min	2.7	%	ISO 527
Tensile Modulus, 1 mm/min	5350	MPa	ISO 527
Flexural Stress	65	MPa	ISO 178
Flexural Modulus, 2 mm/min	4690	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	195	J/m	ASTM D 4812
Izod Impact, notched, 23°C	48	J/m	ASTM D 256
Multiaxial Impact	2	J	ISO 6603
Instrumented Impact Total Energy, 23°C	12	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	13	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	143	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	103	°C	ASTM D 648
CTE, -30°C to 30°C, flow	4.5E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	1.01E-04	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	134	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	95	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.06	-	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.7 - 0.9	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1 - 3	%	ASTM D 955
Density	1.05	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.01	%	ISO 62
Source GMD, last updated:10/03/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	225 - 250	°C
Front - Zone 3 Temperature	240 - 250	°C
Middle - Zone 2 Temperature	215 - 225	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/03/2008