S-Plastic Thermocomp PH0320A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gr

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PH0320A resin is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break	61	MPa	ASTM D 638
Tensile Strain, break	1.4	%	ASTM D 638
Tensile Modulus, 50 mm/min	6040	MPa	ASTM D 638
Flexural Stress	91	MPa	ASTM D 790
Flexural Modulus	5280	MPa	ASTM D 790
Tensile Stress, break	49	MPa	ISO 527
Tensile Strain, break	1.1	%	ISO 527
Tensile Modulus, 1 mm/min	5800	MPa	ISO 527
Flexural Stress	95	MPa	ISO 178
Flexural Modulus	5260	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	261	J/m	ASTM D 4812
Izod Impact, notched, 23°C	26	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	6	J	ASTM D 3763
Multiaxial Impact	2	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	19	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	192	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	86	°C	ASTM D 648
CTE, -40°C to 40°C, flow	5.18E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	6.08E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	5.18E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.07E-05	1/°C	ISO 11359-2
PHYSICAL	Value	Unit	Standard
Density	3.071	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.36	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1.1	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.1	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.08	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.1	%	ISO 294
Density	3.06	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.49	%	ISO 62
Source GMD, last updated:10/01/2004