S-Plastic Thermocomp PH0390A is a compound based on Nylon 6 resin. Added features of this material include: High SpecificGr

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PH0390A resin is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break	56	MPa	ASTM D 638
Tensile Strain, break	2.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	7190	MPa	ASTM D 638
Flexural Stress	100	MPa	ASTM D 790
Flexural Modulus	5870	MPa	ASTM D 790
Tensile Stress, break	53	MPa	ISO 527
Tensile Strain, break	2.9	%	ISO 527
Tensile Modulus, 1 mm/min	6870	MPa	ISO 527
Flexural Stress	101	MPa	ISO 178
Flexural Modulus	6340	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	341	J/m	ASTM D 4812
Izod Impact, notched, 23°C	32	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	7	J	ASTM D 3763
Multiaxial Impact	2	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	26	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	197	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	123	°C	ASTM D 648
CTE, -40°C to 40°C, flow	5.38E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	5.41E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	5.38E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	5.41E-05	1/°C	ISO 11359-2
PHYSICAL	Value	Unit	Standard
Density	3.812	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.18	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1.1	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.1	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.09	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.07	%	ISO 294
Density	3.8	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.43	%	ISO 62
Source GMD, last updated:10/01/2004