S-Plastic Thermocomp PH0400BI is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PH0400BI resin is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity, High Impact.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	35	MPa	ASTM D 638
Tensile Stress, break	35	MPa	ASTM D 638
Tensile Strain, yield	1	%	ASTM D 638
Tensile Strain, break	1.3	%	ASTM D 638
Tensile Modulus, 50 mm/min	12960	MPa	ASTM D 638
Flexural Stress	68	MPa	ASTM D 790
Flexural Modulus	10290	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	260	J/m	ASTM D 4812
Izod Impact, notched, 23°C	58	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	15	J	ASTM D 3763
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	150	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Density	4	g/cm³	ASTM D 792
Mold Shrinkage, xflow, 24 hrs	0.6	%	ASTM D 955
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 270	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	250 - 260	°C
Rear - Zone 1 Temperature	240 - 250	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008