S-Plastic Thermocomp PH0460A is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PH0460A resin is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	59	MPa	ASTM D 638
Tensile Stress, break	56	MPa	ASTM D 638
Tensile Strain, yield	0.9	%	ASTM D 638
Tensile Strain, break	1	%	ASTM D 638
Tensile Modulus, 50 mm/min	9650	MPa	ASTM D 638
Flexural Stress	96	MPa	ASTM D 790
Flexural Modulus	8270	MPa	ASTM D 790
Tensile Stress, yield	55	MPa	ISO 527
Tensile Stress, break	56	MPa	ISO 527
Tensile Strain, yield	0.8	%	ISO 527
Tensile Strain, break	0.8	%	ISO 527
Tensile Modulus, 1 mm/min	8430	MPa	ISO 527
Flexural Stress	93	MPa	ISO 178
Flexural Modulus	7800	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	144	J/m	ASTM D 4812
Izod Impact, notched, 23°C	42	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	7	J	ASTM D 3763
Multiaxial Impact	2	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	16	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	196	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	156	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.32E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	4.2E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.5E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	196	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	149	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	4.51	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.1	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1.1 - 1.3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.1 - 1.3	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.2	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.2	%	ISO 294
Density	4.49	g/cm³	ISO 1183
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 270	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	250 - 260	°C
Rear - Zone 1 Temperature	240 - 250	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008