S-Plastic Thermocomp PX05046 is a compound based on PA 6 resin containing Glass Bead, Glass Fiber. Added features include: H

Name: S-Plastic Thermocomp PX05046 is a compound based on PA 6 resin containing Glass Bead, Glass Fiber. Added features include: H
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PX05046 resin is a compound based on PA 6 resin containing Glass Bead, Glass Fiber. Added features include: Heat

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 5 mm/min	95	MPa	ISO 527
Tensile Strain, break, 5 mm/min	>3	%	ISO 527
Tensile Modulus, 1 mm/min	5800	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	145	MPa	ISO 178
Flexural Modulus, 2 mm/min	4700	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	40	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	175	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow (5)	0.4 - 0.6	%	S-Plastics Method
Density	1.36	g/cm³	ISO 1183
Source GMD, last updated:2009/12/22

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 275	°C
Front - Zone 3 Temperature	275 - 290	°C
Middle - Zone 2 Temperature	265 - 275	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2009/12/22

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Thermocomp PX05046.pdf

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!