S-Plastic Thermocomp NX07354P is a PC/ABS compound with improved plating performance, a good candidate for Laser Direct St

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp NX07354P resin is a PC/ABS compound with improved plating performance, a good candidate for Laser Direct Structuring applications.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	42	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	42	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	3.5	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	72.7	%	ASTM D 638
Tensile Modulus, 50 mm/min	2570	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	73	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	72	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2430	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	41	MPa	ISO 527
Tensile Stress, break, 5 mm/min	40	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	3.4	%	ISO 527
Tensile Strain, break, 5 mm/min	77.8	%	ISO 527
Tensile Modulus, 1 mm/min	2520	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	75	MPa	ISO 178
Flexural Strain, break, 2 mm/min	74.2	%	ISO 178
Flexural Modulus, 2 mm/min	2600	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	530	J/m	ASTM D 256
Izod Impact, notched 80104 +23°C	45	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	96	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.62E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.59E-05	1/°C	ASTM E 831
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	95	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.22	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.05	%	ASTM D 570
Mold Shrinkage, flow (5)	0.69	%	S-Plastics Method
Mold Shrinkage, xflow (5)	0.61	%	S-Plastics Method
Density	1.22	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Relative Permittivity, 1 GHz	2.8	-	ASTM D 150
Dissipation Factor, 1 GHz	0.003	-	ASTM D 150
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.5	mm	UL 94
Source GMD, last updated:2009/09/28

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80 - 90	°C
Drying Time	6 - 8	hrs
Melt Temperature	235 - 255	°C
Nozzle Temperature	235 - 255	°C
Front - Zone 3 Temperature	235 - 255	°C
Middle - Zone 2 Temperature	230 - 245	°C
Rear - Zone 1 Temperature	230 - 245	°C
Mold Temperature	60 - 80	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Source GMD, last updated:2009/09/28