S-Plastics Thermocom OB008 resin is Glass Bead Filled, PPS

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	40	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	40	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.7	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	6630	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	87	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	87	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	5920	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	47	MPa	ISO 527
Tensile Stress, break, 5 mm/min	46	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1	%	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	6330	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	-	MPa	ISO 178
Flexural Strain, break, 2 mm/min	1.7	%	ISO 178
Flexural Modulus, 2 mm/min	6170	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	147	J/m	ASTM D 4812
Izod Impact, notched, 23°C	31	J/m	ASTM D 256
Multiaxial Impact	1	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	9	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	218	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	115	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.3E+01	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.14E+01	1/°C	ASTM E 831
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	202	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	121	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.635	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.01	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.92 - 0.94	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.92 - 0.94	%	ASTM D 955
Density	1.63	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.01	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Dissipation Factor, 50/60 Hz	-	-	ASTM D 150
Source GMD, last updated:12/18/2007

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Melt Temperature	315 - 320	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm