S-Plastic Thermocomp OK006 is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp OK006 resin is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	72	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	72	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.4	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.4	%	ASTM D 638
Tensile Modulus, 50 mm/min	8340	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	112	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	108	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	7300	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	66	MPa	ISO 527
Tensile Stress, break, 5 mm/min	66	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.2	%	ISO 527
Tensile Strain, break, 5 mm/min	1.2	%	ISO 527
Tensile Modulus, 1 mm/min	7790	MPa	ISO 527
Flexural Stress	105	MPa	ISO 178
Flexural Modulus, 2 mm/min	7550	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	211	J/m	ASTM D 4812
Izod Impact, notched, 23°C	25	J/m	ASTM D 256
Multiaxial Impact	1	J	ISO 6603
Instrumented Impact Total Energy, 23°C	8	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	13	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	2	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	244	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	123	°C	ASTM D 648
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	226	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	117	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.59	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.02	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.3 - 0.5	%	ASTM D 955
Density	1.59	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.03	%	ISO 62
Source GMD, last updated:2009/01/08

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Melt Temperature	315 - 320	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2009/01/08