S-Plastic Thermocomp PD000IE4 is a compound based on PA 6 resin containing Carbon Powder. Added features include; Impact Mod

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PD000IE4 resin is a compound based on PA 6 resin containing Carbon Powder. Added features include; Impact Modified,
Easy Molding.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 5 mm/min	47	MPa	ISO 527
Tensile Strain, break, 5 mm/min	25	%	ISO 527
Tensile Modulus, 1 mm/min	2100	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	70	MPa	ISO 178
Flexural Modulus, 2 mm/min	2100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	>70	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	7	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	51	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow (5)	1.6 - 1.8	%	S-Plastics Method
Density	1.18	g/cm³	ISO 1183
Source GMD, last updated:2009/07/28

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 275	°C
Front - Zone 3 Temperature	275 - 290	°C
Middle - Zone 2 Temperature	265 - 275	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2009/07/28

Other related products we recommend:

For more information please download the datasheet

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!