S-Plastic Thermocomp RX06027 resin is a compound based on PA 66 containing Glass Bead. Added features include: Easy Molding,

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp RX06027 resin is a compound based on PA 66 containing Glass Bead. Added features include: Easy Molding, HeatStabilized, UV-Stabilized.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 5 mm/min	50	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.5	%	ISO 527
Tensile Modulus, 1 mm/min	3400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	83	MPa	ISO 178
Flexural Modulus, 2 mm/min	2900	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	25	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	6.7E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	6.7E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	61	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.36	g/cm³	ISO 1183
Source GMD, last updated:02/06/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	280 - 305	°C
Front - Zone 3 Temperature	295 - 305	°C
Middle - Zone 2 Temperature	280 - 295	°C
Rear - Zone 1 Temperature	265 - 275	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:02/06/2008