MECS-Plastic Thermocomp RX07034 resin is a compound based on PA 66 resin containing Glass Fiber. Added features include; Low

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp RX07034 resin is a compound based on PA 66 resin containing Glass Fiber. Added features include; Low Smoke, EasyMolding, Cross Linkable under Beta-or Gamma Radiation; Specially developed for Arc chambers.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	170	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.3	%	ISO 527
Flexural Stress, break, 2 mm/min	225	MPa	ISO 178
Flexural Modulus, 2 mm/min	9500	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	60	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	9	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	213	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow (5)	0.3 - 0.5	%	S-Plastics Method
Density	1.54	g/cm³	ISO 1183
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94HB Flame Class Rating (3)(4)	1.6	mm	UL 94 by GE
Source GMD, last updated:2008/12/05

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.2	%
Melt Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 290	°C
Middle - Zone 2 Temperature	265 - 285	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	60 - 90	°C
Back Pressure	>1	MPa
Screw Speed	80 - 120	rpm
Source GMD, last updated:2008/12/05