S-Plastic Thermocomp RX96592 resin is a compound based on Nylon 6/6 containing Proprietary Fillers.

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp RX96592 resin is a compound based on Nylon 6/6 containing Proprietary Fillers.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	154	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	10300	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	222	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	221	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	9140	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	152	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.2	%	ISO 527
Tensile Modulus, 1 mm/min	10210	MPa	ISO 527
Flexural Stress	218	MPa	ISO 178
Flexural Modulus, 2 mm/min	8810	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	626	J/m	ASTM D 4812
Izod Impact, notched, 23°C	67	J/m	ASTM D 256
Multiaxial Impact	1	J	ISO 6603
Instrumented Impact Total Energy, 23°C	7	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	37	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	255	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	239	°C	ASTM D 648
CTE, -30°C to 30°C, flow	3.81E+01	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	8.96E+01	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	253	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	233	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.39	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.85	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.3 - 0.6	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	1 - 4	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	1.4	%	ISO 62
Source GMD, last updated:2009/09/02