S-Plastic Thermocomp TH0300A resin compound based on Polyurethane resin. Added features of this material include: High S
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Thermocomp
Product Description
S-Plastics Thermocomp TH0300A resin is a compound based on Polyurethane resin. Added features of this material include: High SpecificGravity.
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 13 | MPa | ASTM D 638 |
| Tensile Strain, yield | 53.3 | % | ASTM D 638 |
| Tensile Strain, break | 225.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 230 | MPa | ASTM D 638 |
| Flexural Stress | 12 | MPa | ASTM D 790 |
| Flexural Modulus | 330 | MPa | ASTM D 790 |
| Tensile Stress, yield | 28 | MPa | ISO 527 |
| Tensile Strain, yield | 15 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 390 | MPa | ISO 527 |
| Flexural Stress | 10 | MPa | ISO 178 |
| Flexural Modulus | 400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 517 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 27 | J | ASTM D 3763 |
| Multiaxial Impact | 29 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 32 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 55 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 38 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.15E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.32E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.15E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.33E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 57 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 35 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 2.999 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.25 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 1.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 1.2 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.02 | % | ISO 294 |
| Density | 3.19 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.39 | % | ISO 62 |
| Source GMD, last updated:10/01/2004 | |||
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.03 | % |
| Melt Temperature | 200 - 210 | °C |
| Front - Zone 3 Temperature | 195 - 205 | °C |
| Middle - Zone 2 Temperature | 190 - 200 | °C |
| Rear - Zone 1 Temperature | 180 - 195 | °C |
| Mold Temperature | 15 - 45 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin