S-Plastic Thermocomp TH0300B resin is a compound based on Polyurethane containing proprietary fillers. Characteristics of th

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp TH0300B resin is a compound based on Polyurethane containing proprietary fillers. Characteristics of this grade are HighSpecific Gravity.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	18	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	14	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	11.5	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	31.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	1240	MPa	ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	990	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	18	MPa	ISO 527
Tensile Stress, break, 5 mm/min	15	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	11.5	%	ISO 527
Tensile Strain, break, 5 mm/min	31.3	%	ISO 527
Tensile Modulus, 1 mm/min	1090	MPa	ISO 527
Flexural Stress	18	MPa	ISO 178
Flexural Modulus, 2 mm/min	1090	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1530	J/m	ASTM D 4812
Izod Impact, notched, 23°C	158	J/m	ASTM D 256
Multiaxial Impact	15	J	ISO 6603
Instrumented Impact Total Energy, 23°C	22	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	118	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	15	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	92	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	49	°C	ASTM D 648
CTE, -30°C to 30°C, flow	9.9E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	1.09E-04	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	92	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	48	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	3.02	-	ASTM D 792
Density	3.01	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.14	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.5 - 0.7	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.6 - 0.8	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.21	%	ISO 62
Source GMD, last updated:2010/07/19

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.03	%
Melt Temperature	200 - 210	°C
Front - Zone 3 Temperature	195 - 205	°C
Middle - Zone 2 Temperature	190 - 200	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	15 - 45	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2010/07/19