S-Plastic Thermocomp TH0600A resin is a compound based on Polyurethane resin. Added features of this material include: High

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp TH0600A resin is a compound based on Polyurethane resin. Added features of this material include: High SpecificGravity.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	19	MPa	ASTM D 638
Tensile Stress, break	17	MPa	ASTM D 638
Tensile Strain, yield	14.4	%	ASTM D 638
Tensile Strain, break	25.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	1100	MPa	ASTM D 638
Flexural Stress	22	MPa	ASTM D 790
Flexural Modulus	980	MPa	ASTM D 790
Tensile Stress, yield	17	MPa	ISO 527
Tensile Stress, break	14	MPa	ISO 527
Tensile Strain, yield	11.3	%	ISO 527
Tensile Strain, break	52.1	%	ISO 527
Tensile Modulus, 1 mm/min	920	MPa	ISO 527
Flexural Stress	18	MPa	ISO 178
Flexural Modulus	960	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1367	J/m	ASTM D 4812
Izod Impact, notched, 23°C	299	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	16	J	ASTM D 3763
Multiaxial Impact	12	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	85	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	18	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	71	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	44	°C	ASTM D 648
CTE, -40°C to 40°C, flow	9.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	8.89E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	9.5E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.89E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	75	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	45	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	6.046	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.1	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.8	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.96	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.76	%	ISO 294
Density	6.03	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.18	%	ISO 62
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.03	%
Melt Temperature	200 - 210	°C
Front - Zone 3 Temperature	195 - 205	°C
Middle - Zone 2 Temperature	190 - 200	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	15 - 45	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/01/2004